Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LC1700 IDEMITSU JAPAN
TARFLON™
LCD、application
UV resistance、High mobility、Aging resistance、optical performance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/LC1700
Molding shrinkage rate
ASTM D955
%
0
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
4
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/LC1700
Dissolved volume flow rate
MVR
ISO 1133
cm3/10min
4
Shrinkage rate
TD
Internal Method
%
0
Shrinkage rate
MD: 2.00 mm
Internal Method
%
0
Water absorption rate
平衡,23℃, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/LC1700
elongation at break
ASTM D638/ISO 527
%
t
Fracture rate
ISO 527-2
%
9
Charpy Notched Impact Strength
ISO 179
kJ/m²
4
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
Y
Tensile stress
屈服
ISO 527-2
Mpa
6
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
Bending modulus
ISO 178
Mpa
2
bending strength
ISO 178
Mpa
9
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
9
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
Thermal performance
Test Condition
Test Method
Unit
PC/IDEMITSU JAPAN/LC1700
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
1
Hot deformation temperature
1.8 MPa, 未退火
ISO 75-2/A
°C
1