Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO N190X-701 SABIC INNOVATIVE SHANGHAI
NORYL™
Automotive components、Illuminating lamp
transparent、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/N190X-701
Melt flow rate
280°C/5.0 kg
ASTM D1238
g/10 min
2
Molten Volume Flow Rate (MVR)
280°C/5.0 kg
ISO 1133
cm3/10min
2
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
24 hr
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/N190X-701
Tensile strength
屈服 3
ASTM D638
Mpa
6
Tensile strength
屈服
ISO 527-2/50
Mpa
5
Tensile strength
断裂 3
ASTM D638
Mpa
4
Tensile strength
断裂
ISO 527-2/50
Mpa
5
Tensile modulus
-- 2
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
elongation
屈服 3
ASTM D638
%
3
elongation
屈服
ISO 527-2/50
%
3
elongation
断裂 3
ASTM D638
%
9
elongation
断裂
ISO 527-2/50
%
9
Taber abraser
1000 Cycles, 1000 g, CS-17 转轮
ASTM D1044
mg
7
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending modulus
100 mm 跨距 5
ASTM D790
Mpa
2
Bending modulus
-- 6
ISO 178
Mpa
2
Bending stress
-- 6, 7
ISO 178
Mpa
8
Bending stress
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
9
Bending stress
屈服, 100 mm 跨距 5
ASTM D790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/N190X-701
RTI
UL 746
°C
9
RTI Elec
UL 746
°C
9
RTI Imp
UL 746
°C
8
thermal conductivity
ASTM C177
W/m/K
0
Vicat softening temperature
--
ASTM D15259
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
8
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
9
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8
ISO 75-2/Bf
°C
9
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
7
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
8
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8
ISO 75-2/Af
°C
8
Electrical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/N190X-701
Dielectric strength
3.20 mm, in Oil
ASTM D149
KV/mm
1
Volume resistivity
ASTM D257
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/N190X-701
Non notched cantilever beam impact
23°C
ASTM D4812
J/m
7
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
5
flammability
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/N190X-701
Extreme Oxygen Index
ASTM D2863
%
3