Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA610 QFL-4036 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical tools、Electronic and Electrical
Thermal stability、Conductive、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA610/SABIC INNOVATIVE US/QFL-4036
Shrinkage rate
TD:24小时
ASTMD955
%
0
Shrinkage rate
TD:24小时
ISO294-4
%
0
Shrinkage rate
MD:24小时
ISO294-4
%
0
Shrinkage rate
MD:24小时
ASTMD955
%
0
Water absorption rate
24hr,50%RH
ASTMD570
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA610/SABIC INNOVATIVE US/QFL-4036
Tensile strength
断裂
ASTMD638
Mpa
1
Tensile strength
断裂
ISO527-2
Mpa
1
Tensile modulus
--3
ASTMD638
Mpa
1
Tensile modulus
--
ISO527-2/1
Mpa
9
Wear factor - Washer
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
1
elongation
断裂
ASTMD638,ISO527-2
%
2
Bending modulus
--
ASTMD790
Mpa
8
Bending modulus
--
ISO178
Mpa
9
bending strength
--
ASTMD790
Mpa
2
bending strength
--
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA610/SABIC INNOVATIVE US/QFL-4036
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,64.0mm跨距5
ISO75-2/Af
°C
2
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831,ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD:-40到40°C
ISO11359-2
cm/cm/°C
7
Impact performance
Test Condition
Test Method
Unit
PA610/SABIC INNOVATIVE US/QFL-4036
Cantilever beam without notch impact strength
23°C
ASTMD4812
J/m
9
Cantilever beam without notch impact strength
23°C4
ISO180/1U
kJ/m²
6
Dart impact equipped with measuring instruments
23°C,EnergyatPeakLoad
ASTMD3763
J
8
Dart impact equipped with measuring instruments
--
ISO6603-2
J
3