Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL1414 WH9A320 SABIC INNOVATIVE NANSHA
LEXAN™
Electrical applications、Home appliance components、Fitness equipment
Processability、Moderate liquidity、Ductility、copolymer、Good demolding performanc
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Density/specific gravity
ASTMD792
g/cm³
1
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
9
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Tensile strength 3
屈服
ASTMD638
Mpa
5
Tensile strength 3
断裂
ASTMD638
Mpa
5
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus 2
ASTMD638
Mpa
2
Tensile strain
屈服
ISO527-2/50
%
6
Tensile strain
断裂
ISO527-2/50
%
1
Tensile stress
断裂
ISO527-2/50
Mpa
6
Tensile stress
屈服
ISO527-2/50
Mpa
5
Elongation rate 3
屈服
ASTMD638
%
6
Elongation rate 4
断裂
ASTMD638
%
9
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus 5
ISO178
Mpa
2
Bending strength 4
屈服,50.0mm跨距
ASTMD790
Mpa
9
Bending strength 5,6
ISO178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414 WH9A320
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
RTIStr
UL746
°C
1
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 9
1.8MPa,Unannealed,100mmSpan
ISO75-2/Ae
°C
1
Hot deformation temperature 9
0.45MPa,Unannealed,100mmSpan
ISO75-2/Be
°C
1
Vicat softening temperature
ASTMD152510
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
MD：23到80°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：23to80°C
ISO11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Surface resistivity
ASTMD257
ohms
>
Dielectric strength
0.800mm,inOil
ASTMD149
KV/mm
1
Volume resistivity
ASTMD257
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Impact strength of simply supported beam gap 7
-30°C
ISO179/1eA
kJ/m²
6
Impact strength of simply supported beam gap 7
23°C
ISO179/1eA
kJ/m²
7
Impact strength of cantilever beam gap
-30°C
ASTMD256
J/m
7
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
8
Suspended wall beam gap impact strength 8
-30°C
ISO180/1A
kJ/m²
6
Suspended wall beam gap impact strength 8
23°C
ISO180/1A
kJ/m²
7
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
7
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/EXL1414 WH9A320
Hot filament ignition temperature
1.0mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
8
Burning wire flammability index
0.8mm
IEC60695-2-12
°C
8
Burning wire flammability index
1.0mm
IEC60695-2-12
°C
9