Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-765B TAIWAN CHIMEI
POLYLAC®
Electrical tools、Electrical field、Electronic field、Home appliance components
Flame retardant、Medium impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-765B
Density/specific gravity
--3
ASTMD792
g/cm³
1
Density/specific gravity
23°C
ISO1183
g/cm³
1
Melt volume flow rate
220°C/10.0kg
ISO1133
cm3/10min
3
Melt mass flow rate
200°C/5.0kg
ASTMD1238
g/10min
4
Shrinkage rate
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-765B
Tensile strength
屈服4
ASTMD638
Mpa
3
Tensile strength
屈服
ISO527-2/50
Mpa
3
Tensile strength
断裂
ISO527-2/50
Mpa
2
elongation
断裂4
ASTMD638
%
2
elongation
断裂
ISO527-2/50
%
1
Bending modulus
--5
ASTMD790
Mpa
2
Bending modulus
--6
ISO178
Mpa
1
bending strength
--5
ASTMD790
Mpa
6
bending strength
--6
ISO178
Mpa
5
Thermal performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-765B
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
7
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
7
Hot deformation temperature
1.8MPa,退火
ASTMD648,ISO75-2/A
°C
8
Vicat softening temperature
--
ASTMD15257
°C
9
Vicat softening temperature
--
ISO306/A50
°C
9
Vicat softening temperature
--
ISO306/B50
°C
8
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
8
Impact performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-765B
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
1
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
2
Impact strength of cantilever beam gap
23°C,3.20mm
ASTMD256
J/m
2
Impact strength of cantilever beam gap
23°C,6.40mm
ASTMD256
J/m
2
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
1
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
2