LCP T130 CELANESE USA
VECTRA®
Home appliance components、Automotive Applications
heat-resisting、enhance、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
LCP/CELANESE USA/T130
Shrinkage rate
normal
ISO 2577
%
0
Shrinkage rate
parallel
ISO 2577
%
0
Mechanical performance
Test Condition
Test Method
Unit
LCP/CELANESE USA/T130
Charpy Notched Impact Strength
23℃
ISO 179/1eA
KJ/m
9
Impact strength of simply supported beam without notch
23℃
ISO 179/1eU
KJ/m
2
Impact strength of simply supported beam without notch
-30℃
ISO 179/1eU
KJ/m
5
Tensile modulus
ISO 527-1,-2/1
Mpa
1
tensile strength
ISO 527-1,-2/5
Mpa
1
Tensile creep modulus
1hr
ISO 899-1
Mpa
9
Tensile creep modulus
1000hr
ISO 899-1
Mpa
6
elongation
断裂
ISO 527-1,-2/5
%
3
Bending modulus
23℃
ISO 178
Mpa
9
bending strength
23℃
ISO 178
Mpa
1
Impact strength of cantilever beam gap
23℃
ISO 180/1A
KJ/m
9
Cantilever beam without notch impact strength
23℃
ISO 180/1U
KJ/m
2
Thermal performance
Test Condition
Test Method
Unit
LCP/CELANESE USA/T130
Hot deformation temperature
1.80MPa
ISO 75-1,-2
°C
1
Hot deformation temperature
8.00MPa
ISO 75-1,-2
°C
1
Vicat softening temperature
50℃/h 50N
ISO 306
°C
1
Linear coefficient of thermal expansion
parallel
ISO 11359-1,-2
cm/cm℃
4
Linear coefficient of thermal expansion
normal
ISO 11359-1,-2
cm/cm℃
0
Electrical performance
Test Condition
Test Method
Unit
LCP/CELANESE USA/T130
Surface resistivity
IEC 60093
ohms
1
Electrical strength
IEC 60243-1
KV/mm
4
Volume resistivity
IEC 60093
ohm.m
1
Basic performance
Test Condition
Test Method
Unit
LCP/CELANESE USA/T130
density
ISO 1183
kg/m
1
Water absorption rate
23℃/50rh
ISO 62
%
0