Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GS2010MR2 MITSUBISHI ENGINEERING JAPAN
IUPILON™
fibre
Flame retardant、enhance、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/GS2010MR2
Molding shrinkage rate
ASTM D955
%
0
physical property
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/GS2010MR2
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
9
Melt mass flow rate
300°C/1.2kg
ISO1133
g/10min
1
Water absorption rate
饱和,23°C
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/GS2010MR2
elongation at break
ASTM D638/ISO 527
%
3
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
4
Tensile modulus
ISO527-2
Mpa
4
Tensile strain
断裂
ISO527-2
%
2
Tensile stress
断裂
ISO527-2
Mpa
7
Bending modulus
ISO178
Mpa
4
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
3
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Bending stress
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/GS2010MR2
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
4
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
6
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
4
Impact performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/GS2010MR2
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
5