PPS OL-4030 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive Applications
Carbon fiber reinforced、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OL-4030
Shrinkage rate
MD：24小时
ASTMD955
%
0
Shrinkage rate
TD：24hr
ASTMD955
%
1
Water absorption rate
24hr,50%RH
ASTMD570
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OL-4030
Tensile strength 3
断裂
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/1
Mpa
3
Tensile modulus 2
ASTMD638
Mpa
3
Tensile strain
断裂
ISO527-2/5
%
0
Tensile stress
断裂
ISO527-2/5
Mpa
2
Elongation rate 4
断裂
ASTMD638
%
0
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
3
Bending modulus 5
ISO178
Mpa
3
Bending strength 5
断裂,50.0mm跨距
ASTMD790
Mpa
6
Bending stress
ISO178
Mpa
5
Thermal performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OL-4030
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 7
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
1
Hot deformation temperature 7
1.8MPa,未退火,64.0mm跨距
ISO75-2/Af
°C
1
Linear coefficient of thermal expansion
MD：-30到30°C
ASTMD696
cm/cm/°C
6
Linear coefficient of thermal expansion
TD：-30to30°C
ASTMD696
cm/cm/°C
6
Impact performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OL-4030
Multi axis Instrumented Impact Energy
ISO6603-2
J
0
Unscented Izod Impact Strength 5
23°C
ISO180/1U
kJ/m²
4
Suspended wall beam notch impact strength 6
23°C
ISO180/1A
kJ/m²
2
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
1