Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC CF-3300LW Samsung Cheil South Korea
INFINO®
Electronic and Electrical、Phone
High rigidity、Antichemical、Filler: Glass fiber reinf、Filler: Glass fiber reinf、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/Samsung Cheil South Korea/CF-3300LW
Density/specific gravity
ASTMD792
g/cm³
1
Density/specific gravity
ISO1183
g/cm³
1
Melt mass flow rate
250°C/10.0kg
ASTMD1238
g/10min
2
Melt mass flow rate
250°C/10.0kg
ISO1133
g/10min
2
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD:3.20mm
ISO2577
%
0
Shrinkage rate
MD:3.20mm
ISO2577
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/Samsung Cheil South Korea/CF-3300LW
Tensile strength 2
屈服
ASTMD638
Mpa
1
Tensile strength 2
断裂
ASTMD638
Mpa
1
Tensile modulus
ISO527-2/50
Mpa
6
Tensile modulus 2
ASTMD638
Mpa
6
Tensile strain
断裂
ISO527-2/50
%
3
Tensile stress
屈服
ISO527-2/50
Mpa
1
Tensile stress
断裂
ISO527-2/50
Mpa
1
Elongation rate 2
断裂
ASTMD638
%
3
Bending modulus 3
ASTMD790
Mpa
6
Bending modulus 4
ISO178
Mpa
7
Bending strength 3
ASTMD790
Mpa
1
Bending stress 5
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/Samsung Cheil South Korea/CF-3300LW
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,Unannealed,4.00mm
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Impact performance
Test Condition
Test Method
Unit
PC/Samsung Cheil South Korea/CF-3300LW
CharpyNotchedImpactStrength6
23°C
ISO179/1eA
kJ/m²
1
Impact strength of cantilever beam gap
23°C,3.18mm
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C,6.35mm
ASTMD256
J/m
1
Suspended wall beam notch impact strength 6
23°C
ISO180/1A
kJ/m²
1