Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP G3230A-10000 SABIC INNOVATIVE US
SABIC®
Engine hood parts
Homopolymer、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PP/SABIC INNOVATIVE US/G3230A-10000
Melt mass flow rate
230°C/2.16kg
ISO1133
g/10min
1
Shrinkage rate
TD:23°C,48小时
内部方法
%
0
Shrinkage rate
MD:23°C,48小时
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PP/SABIC INNOVATIVE US/G3230A-10000
Tensile strength 3
断裂
ASTMD638
Mpa
8
Tensile modulus
ISO527-2/1
Mpa
6
Tensile modulus 2
ASTMD638
Mpa
6
Tensile strain
断裂
ISO527-2/50
%
3
Tensile stress
断裂
ISO527-2/1A/50
Mpa
8
Elongation rate 4
断裂
ASTMD638
%
2
Bending modulus
50.0mm跨距4
ASTMD790
Mpa
5
Bending modulus
50.0mm跨距5
ISO178
Mpa
6
Thermal performance
Test Condition
Test Method
Unit
PP/SABIC INNOVATIVE US/G3230A-10000
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 6
1.8MPa,Unannealed
ISO75-2/A
°C
1
Hot deformation temperature 6
0.45MPa,Unannealed
ISO75-2/B
°C
1
Vicat softening temperature
ISO306/A50
°C
1
Linear coefficient of thermal expansion
MD：-30到100°C
ISO11359-2
cm/cm/°C
5
Linear coefficient of thermal expansion
TD：-30to100°C
ISO11359-2
cm/cm/°C
1
Impact performance
Test Condition
Test Method
Unit
PP/SABIC INNOVATIVE US/G3230A-10000
Gardner Impact10
23°C
ASTMD5420
J
0
InstrumentedDartImpact9
23°C,EnergyatPeakLoad
ASTMD3763
J
7
NotchedIzodImpact8
23°C,3.20mm
ASTMD256
J/m
8
Suspended wall beam notch impact strength 6
-30°C
ISO180/1A
kJ/m²
1
Suspended wall beam notch impact strength 6
23°C
ISO180/1A
kJ/m²
1
Cantilever beam without notch impact strength 8
23°C,3.20mm
ASTMD4812
J/m
5