Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA HTN51G15HSL DUPONT USA
Zytel®
Cable、Electric wire
enhance、Glass fiber reinforced、Weather resistance、Thermal stability、Low temperature resistanc、High temperature resistan、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPA/DUPONT USA/HTN51G15HSL
Density/specific gravity
ISO1183
g/cm³
1
Shrinkage rate
TD
ISO294-4
%
0
Shrinkage rate
MD
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPA/DUPONT USA/HTN51G15HSL
Tensile modulus 2
ISO527-2
Mpa
6
Tensile strain 2
断裂
ISO527-2
%
2
Tensile stress 2
断裂
ISO527-2
Mpa
1
Bending modulus
ISO178
Mpa
5
Thermal performance
Test Condition
Test Method
Unit
PPA/DUPONT USA/HTN51G15HSL
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature 5
ISO11357-3
°C
3
Linear coefficient of thermal expansion
MD：--
ISO11359-2
cm/cm/°C
3
Linear coefficient of thermal expansion
MD：-40to23°C
ISO11359-2
cm/cm/°C
5
Linear coefficient of thermal expansion
TD：--
ISO11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
TD：-40to23°C
ISO11359-2
cm/cm/°C
3
Linear coefficient of thermal expansion
TD：55to160°C
ISO11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PPA/DUPONT USA/HTN51G15HSL
Surface resistivity
IEC60093
ohms
-
Leakage Trace Index
IEC60112
V
6
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PPA/DUPONT USA/HTN51G15HSL
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
6
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
6
Impact strength of simply supported beam without notch
-30°C2
ISO179/1eU
kJ/m²
2
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
2
Impact strength of cantilever beam gap
-40°C
ISO180/1A
kJ/m²
6
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
6
flammability
Test Condition
Test Method
Unit
PPA/DUPONT USA/HTN51G15HSL
Extreme Oxygen Index
ISO4589-2
%
2
Burning rate 4
1.00mm
ISO3795
mm/min
<