Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B3WG3 BASF GERMANY
Ultramid®
Engine parts、Shell
Thermal stability、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B3WG3
Molding shrinkage rate
ASTM D955
%
0
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
8
Mechanical performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B3WG3
elongation at break
ASTM D638/ISO 527
%
3
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
5
Tensile modulus
23°C
ISO527-2
Mpa
5
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Tensile yield stress
干燥
MPa
130
I
Tensile strain
断裂,23°C
ISO527-2
%
3
Tensile stress
断裂,23°C
ISO527-2
Mpa
1
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
5
Bending modulus
23°C
ISO178
Mpa
5
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
干燥
MPa
180
I
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
6
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
5
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
5
Thermal performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B3WG3
RTIElec
0.8mm
UL746
°C
1
RTIElec
1.5mm
UL746
°C
1
RTIElec
3.0mm
UL746
°C
1
Evolution Calendar intelligent importer
1.5mm
UL746
°C
8
Evolution Calendar intelligent importer
3.0mm
UL746
°C
8
RTIStr
1.5mm
UL746
°C
1
RTIStr
3.0mm
UL746
°C
1
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
1
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Hot deformation temperature
1.8Mpa
℃
190
I
Hot deformation temperature
0.45Mpa
℃
215
I
Melting temperature (DSC)
ISO3146
°C
2
Electrical performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B3WG3
Dielectric loss factor
10
250
I
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
>
Impact performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B3WG3
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
4