density

ASTMD792

g/cm³

1

density

ISO1183

g/cm³

1

Water absorption rate

饱和

ASTMD570

%

4

Water absorption rate

平衡,23°C,50%RH

ISO62

%

1

Water absorption rate

饱和,23°C

ISO62

%

4

Water absorption rate

平衡,50%RH

ASTMD570

%

1

Tensile strength

断裂,23°C

ASTMD638

Mpa

2

Tensile modulus

23°C

ISO527-2

Mpa

1

Tensile strain

断裂,23°C

ISO527-2

%

2

Tensile stress

断裂,23°C

ISO527-2

Mpa

2

elongation

断裂,23°C

ASTMD638

%

2

Bending modulus

23°C

ASTMD790

Mpa

1

Bending modulus

23°C

ISO178

Mpa

1

Bending stress

23°C

ISO178

Mpa

3

RTIElec

0.75mm

UL746

°C

6

RTIElec

3.0mm

UL746

°C

1

RTIElec

1.7mm

UL746

°C

1

Evolution Calendar intelligent importer

1.7mm

UL746

°C

1

Evolution Calendar intelligent importer

0.75mm

UL746

°C

6

Evolution Calendar intelligent importer

3.0mm

UL746

°C

1

RTIStr

0.75mm

UL746

°C

6

RTIStr

1.7mm

UL746

°C

1

RTIStr

3.0mm

UL746

°C

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

2

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

2

Melting temperature (DSC)

ISO3146

°C

2

Peak melting temperature

ASTMD3418

°C

2

VolumeResistivity

1.50mm

ASTMD257

ohms·cm

>

Volume resistivity

IEC60093

ohms·cm

>

Charpy Notched Impact Strength

23°C

ISO179

kJ/m²

1

Impact strength of simply supported beam without notch

23°C

ISO179

kJ/m²

7

Impact strength of cantilever beam gap

-40°C

ISO180

kJ/m²

1

Impact strength of cantilever beam gap

23°C

ASTMD256

J/m

1

Impact strength of cantilever beam gap

23°C

ISO180

kJ/m²

1