Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LUX9612 SABIC INNOVATIVE NANSHA
LEXAN™
Home appliance components、Automotive sector、Lighting applications
optical performance 、UV resistance、Weather resistance、transparent、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9612
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
7
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9612
--
ISO527-2/1
Mpa
2
--1
ASTMD638
Mpa
2
50.0mm span 6
ASTMD790
Mpa
2
--7
ISO178
Mpa
2
--8
ISO178
Mpa
9
crack
ISO527-2/50
Mpa
5
crack
ISO527-2/50
%
7
Fracture 3
ASTMD638
Mpa
6
Fracture 5
ASTMD638
%
8
yield
ISO527-2/50
%
6
yield
ISO527-2/50
Mpa
6
Yield, 50.0mm span 9
ASTMD790
Mpa
9
Surrender 2
ASTMD638
Mpa
6
Surrender 4
ASTMD638
%
6
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9612
0.45MPa, unannealed, 64.0mm span 11
ISO75-2/Bf
°C
1
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
1
1.8MPa, unannealed, 64.0mm span 12
ISO75-2/Af
°C
1
Vicat softening temperature
ASTMD152513
°C
1
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831
cm/cm/°C
6
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831
cm/cm/°C
6
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9612
23°C
ASTMD256
J/m
4
23°C10
ISO180/1A
kJ/m²
4
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
7
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9612
Hot filament ignition temperature
1.00mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
1.50mm
IEC60695-2-13
°C
8
Burning wire flammability index
1.00mm
IEC60695-2-12
°C
9