Melt flow rate

300°C/1.2 kg

ASTM D1238

g/10 min

5

Molten Volume Flow Rate (MVR)

300°C/1.2 kg

ISO 1133

cm3/10min

5

Shrinkage rate - flow

3.20 mm

内部方法

%

0

Water absorption rate

饱和, 23°C

ISO 62

%

0

Water absorption rate

平衡, 23°C, 50% RH

ISO 62

%

0

Tensile strength

屈服 3

ASTM D638

Mpa

6

Tensile strength

屈服

ISO 527-2/50

Mpa

6

Tensile strength

断裂 3

ASTM D638

Mpa

5

Tensile strength

断裂

ISO 527-2/50

Mpa

5

Tensile modulus

-- 2

ASTM D638

Mpa

2

Tensile modulus

--

ISO 527-2/1

Mpa

2

elongation

屈服 3

ASTM D638

%

5

elongation

屈服

ISO 527-2/50

%

6

elongation

断裂 3

ASTM D638

%

1

elongation

断裂

ISO 527-2/50

%

1

Bending modulus

50.0 mm 跨距 4

ASTM D790

Mpa

2

Bending modulus

-- 5

ISO 178

Mpa

2

Bending stress

-- 5, 6

ISO 178

Mpa

9

Bending stress

屈服, 50.0 mm 跨距 4

ASTM D790

Mpa

1

Vicat softening temperature

--

ASTM D152510

°C

1

Vicat softening temperature

--

ISO 306/B50

°C

1

Vicat softening temperature

--

ISO 306/B120

°C

1

Linear coefficient of thermal expansion

流动 : -40 到 40°C

ASTM E831, ISO 11359-2

cm/cm/°C

8

Linear coefficient of thermal expansion

横向 : -40 到 40°C

ASTM E831

cm/cm/°C

8

Linear coefficient of thermal expansion

横向 : -40°C

ISO 11359-2

cm/cm/°C

8

Thermal deformation temperature under load

0.45 MPa, 未退火, 3.20 mm

ASTM D648

°C

1

Thermal deformation temperature under load

1.8 MPa, 未退火, 3.20 mm

ASTM D648

°C

1

Thermal deformation temperature under load

1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9

ISO 75-2/Af

°C

1

Impact strength of simply supported beam gap 7

-30°C

ISO 179/1eA

kJ/m²

1

Impact strength of simply supported beam gap 7

23°C

ISO 179/1eA

kJ/m²

6

Dart impact equipped with measuring instruments

23°C, Total Energy

ASTM D3763

J

5

Dart impact equipped with measuring instruments

--

ISO 6603-2

J

9

transmissivity

2540 µm

ASTM D1003

%

8

Haze

2540 µm

ASTM D1003

%

<