PA66 A3EG6 BASF GERMANY
Ultramid®
Electrical components、Electronic insulation、machine、Mechanical components、Shell
High rigidity、Oil resistant、dimensional stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3EG6
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
4
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
5
physical property
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3EG6
Melt volume flow rate
275°C/5.0kg
ISO1133
cm3/10min
4
Water absorption rate
饱和
ASTMD570
%
5
Water absorption rate
饱和,23°C
ISO62
%
5
Water absorption rate
平衡,50%RH
ASTMD570
%
1
Water absorption rate
平衡,23°C,50%RH
ISO62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3EG6
elongation at break
ASTM D638/ISO 527
%
3
Tensile strength
断裂,23°C
ASTMD638
Mpa
1
Tensile modulus
23°C
ISO527-2
Mpa
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Tensile strain
断裂,-40°C
ISO527-2
%
3
Tensile strain
断裂,23°C
ISO527-2
%
3
Tensile stress
断裂,-40°C
ISO527-2
Mpa
2
Tensile stress
断裂,23°C
ISO527-2
Mpa
1
elongation
断裂,23°C
ASTMD638
%
3
Bending modulus
23°C
ISO178
Mpa
8
Bending modulus
ASTM D790/ISO 178
kg·cm/cm(J/M)ft·lb/in
8
bending strength
ASTM D790/ISO 178
kg·cm/cm(J/M)ft·lb/in
2
Bending stress
23°C
ISO178
Mpa
2
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
Thermal performance
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3EG6
RTIElec
0.75mm
UL746
°C
1
RTIElec
1.5mm
UL746
°C
1
RTIElec
3.0mm
UL746
°C
1
RTIElec
6.0mm
UL746
°C
1
Evolution Calendar intelligent importer
1.5mm
UL746
°C
1
Evolution Calendar intelligent importer
3.0mm
UL746
°C
1
Evolution Calendar intelligent importer
6.0mm
UL746
°C
1
RTIStr
1.5mm
UL746
°C
1
RTIStr
3.0mm
UL746
°C
1
RTIStr
6.0mm
UL746
°C
1
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Hot deformation temperature
0.45MPa,未退火
ASTMD648
°C
2
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature (DSC)
ISO3146
°C
2
Peak melting temperature
ASTMD3418
°C
2
Linear coefficient of thermal expansion
MD
ASTME831
cm/cm/°C
1
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
1
Electrical performance
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3EG6
VolumeResistivity
1.50mm
ASTMD257
ohms·cm
1
Surface resistivity
ASTM D257/IEC 60093
Ω
1
Leakage Trace Index
IEC60112
V
5
Volume resistivity
IEC60093
ohms·cm
1
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
1
Impact performance
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3EG6
Impact strength of simply supported beam without notch
-30°C
ISO179
kJ/m²
7
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
8