Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PTFE NL001 WH8A511 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PTFE/SABIC INNOVATIVE US/NL001 WH8A511
Molten Volume Flow Rate (MVR)
260°C/5.0 kg
ISO 1133
cm3/10min
2
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PTFE/SABIC INNOVATIVE US/NL001 WH8A511
Tensile strength
屈服 3
ASTM D638
Mpa
5
Tensile strength
屈服
ISO 527-2/5
Mpa
4
Tensile strength
屈服
ISO 527-2/50
Mpa
5
Tensile strength
断裂 3
ASTM D638
Mpa
4
Tensile strength
断裂
ISO 527-2/5, ISO 527-2/50
Mpa
4
Tensile modulus
-- 2
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
elongation
屈服 3
ASTM D638
%
3
elongation
屈服
ISO 527-2/5, ISO 527-2/50
%
4
elongation
断裂 3
ASTM D638
%
2
elongation
断裂
ISO 527-2/5
%
4
elongation
断裂
ISO 527-2/50
%
2
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending modulus
-- 5
ISO 178
Mpa
2
Bending stress
-- 5, 6
ISO 178
Mpa
8
Bending stress
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PC/PTFE/SABIC INNOVATIVE US/NL001 WH8A511
Vicat softening temperature
--
ISO 306/B50
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : 23 到 80°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : 23 到 80°C
ISO 11359-2
cm/cm/°C
8
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8
ISO 75-2/Bf
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
9
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9
ISO 75-2/Ae
°C
9
Electrical performance
Test Condition
Test Method
Unit
PC/PTFE/SABIC INNOVATIVE US/NL001 WH8A511
Surface resistivity
IEC 60093
ohms
>
Volume resistivity
IEC 60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/PTFE/SABIC INNOVATIVE US/NL001 WH8A511
Impact strength of simply supported beam gap 7
-30°C
ISO 179/1eA
kJ/m²
1
Impact strength of simply supported beam gap 7
23°C
ISO 179/1eA
kJ/m²
1
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
4
flammability
Test Condition
Test Method
Unit
PC/PTFE/SABIC INNOVATIVE US/NL001 WH8A511
Extreme Oxygen Index
ISO 4589-2
%
2