Shrinkage rate

MD:23°C,2.00mm

ISO294-4

%

0

Shrinkage rate

TD:23°C,2.00mm

ISO294-4

%

1

Water absorption rate

23°C,24hr

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

1

Tensile modulus

23°C

ISO527-2

Mpa

9

Tensile strain

断裂,23°C

ISO527-2

%

2

Tensile stress

断裂,23°C

ISO527-2

Mpa

1

Bending modulus

23°C

ISO178

Mpa

8

bending strength

23°C

ISO178

Mpa

1

RTIElec

0.40mm

UL746

°C

6

RTIElec

0.75mm

UL746

°C

1

RTIElec

1.5mm

UL746

°C

1

RTIElec

3.0mm

UL746

°C

1

Evolution Calendar intelligent importer

0.40mm

UL746

°C

6

Evolution Calendar intelligent importer

0.75mm

UL746

°C

6

Evolution Calendar intelligent importer

1.5mm

UL746

°C

9

Evolution Calendar intelligent importer

3.0mm

UL746

°C

9

RTIStr

0.40mm

UL746

°C

6

RTIStr

0.75mm

UL746

°C

1

RTIStr

1.5mm

UL746

°C

1

RTIStr

3.0mm

UL746

°C

1

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

2

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

2

Melting temperature

ISO11357-3

°C

2

Linear coefficient of thermal expansion

MD：23to55°C,2.00mm

ISO11359-2

cm/cm/°C

2

Linear coefficient of thermal expansion

TD：23to55°C,2.00mm

ISO11359-2

cm/cm/°C

1

Leakage Trace Index

3.00mm

IEC60112

V

2

Impact strength of simply supported beam without notch

-30°C

ISO179/1eU

kJ/m²

3

Impact strength of simply supported beam without notch

23°C

ISO179/1eU

kJ/m²

4

Extreme Oxygen Index

ISO4589-2

%

3

Hot filament ignition temperature

0.40mm

IEC60695-2-13

°C

9

Hot filament ignition temperature

0.75mm

IEC60695-2-13

°C

7

Hot filament ignition temperature

1.5mm

IEC60695-2-13

°C

7

Hot filament ignition temperature

3.0mm

IEC60695-2-13

°C

8

Burning wire flammability index

0.40mm

IEC60695-2-12

°C

9

Burning wire flammability index

0.75mm

IEC60695-2-12

°C

9

Burning wire flammability index

1.5mm

IEC60695-2-12

°C

9

Burning wire flammability index

3.0mm

IEC60695-2-12

°C

9