Specific gravity

ISO 1183

kg/m3

1

Melt index

300°C 1.2kg

ISO 1133

cm3/10min

9

Vertical shrinkage rate

ISO 2577

%

0

Shrinkage rate flow

ISO 2577

%

0

Simply supported beam notch impact -10 ° C

ISO 179

kJ/m²

5

Impact of simply supported beam gap at 23 ° C

ISO 179

kJ/m²

6

Simply supported beam notch impact -30 ° C

ISO 179

kJ/m²

2

Anti puncture 23 ° C

ISO 6603

J

5

Anti puncture -30 ° C

ISO 6603

J

5

Maximum puncture resistance at 23 ° C

ISO 6603

N

5

Maximum puncture resistance -30 ° C

ISO 6603

N

6

Tensile modulus

0mm/min

ISO 527

Mpa

2

Tensile strength fracture 50mm/min

ISO 527

Mpa

6

Tensile strength yield 50mm/min

ISO 527

Mpa

6

Elongation fracture 50mm/min

ISO 527

%

5

Elongation fracture 50mm/min

ISO 527

%

1

Elongation yield 50mm/min

ISO 527

%

6

Bending modulus 2.0mm/min

ISO 178

Mpa

2

Bending strength 2.0mm/min

ISO 178

Mpa

9

Cantilever beam notch impact -10 ° C 3.0mm

ISO 180

kJ/m²

5

Cantilever beam notch impact at 23 ° C 3.0mm

ISO 180

kJ/m²

6

Cantilever beam notch impact -30 ° C 3.0mm

ISO 180

kJ/m²

1

Ball pressure test

ISO 11359-2

°C

1

Hot deformation temperature 0.45MPa

ISO 75

°C

1

Hot deformation temperature 1.8MPa

ISO 75

°C

1

Vicat softening temperature 120 ° C/hr 50N

ISO 306

°C

1

Vicat softening temperature 50 ° C/hr 50N

ISO 306

°C

1

Vertical coefficient of linear expansion 23~55 ° C

ISO 11359

cm/cm/°C

0

Linear expansion coefficient flow 23~55 ° C

ISO 11359

cm/cm/°C

0

CTI solution A

IEC 60112

V

2

Surface resistance

IEC 60093

Ω

4

Volume resistance

IEC 60093

Ω.m

9