Melt flow rate

300°C/1.2 kg

ASTM D1238

g/10 min

1

Shrinkage rate - flow

3.20 mm

内部方法

%

0

Specific volume

ASTM D792

cm³/g

0

Water absorption rate

24 hr

ASTM D570

%

0

Water absorption rate

平衡, 23°C

ASTM D570

%

0

Water absorption rate

平衡, 100°C

ASTM D570

%

0

Tensile strength 2

屈服

ASTM D638

Mpa

6

Tensile strength 2

断裂

ASTM D638

Mpa

6

Elongation rate 2

屈服

ASTM D638

%

7

Elongation rate 2

断裂

ASTM D638

%

1

Taber abraser

1000 Cycles, 1000 g, CS-17 转轮

ASTM D1044

mg

1

Bending modulus

50.0 mm 跨距

ASTM D790

Mpa

2

bending strength

屈服, 50.0 mm 跨距

ASTM D790

Mpa

9

RTI

UL 746

°C

1

RTI Elec

UL 746

°C

1

RTI Imp

UL 746

°C

1

specific heat

ASTM C351

J/kg/°C

1

thermal conductivity

ASTM C177

W/m/K

0

Vicat softening temperature

ASTM D15257

°C

1

Linear coefficient of thermal expansion - flow

-40 到 95°C

ASTM E831

cm/cm/°C

6

Thermal deformation temperature under load

0.45 MPa, 未退火, 6.40 mm

ASTM D648

°C

1

Thermal deformation temperature under load

1.8 MPa, 未退火, 6.40 mm

ASTM D648

°C

1

Dielectric strength

3.20 mm, in Air

ASTM D149

KV/mm

1

Volume resistivity

ASTM D257

ohms·cm

>

Impact strength of simply supported beam gap 4

-30°C

ISO 179/1eA

kJ/m²

1

Impact strength of simply supported beam gap 4

23°C

ISO 179/1eA

kJ/m²

6

Tensile impact strength 6

ASTM D1822

kJ/m²

5

Falling hammer impact

23°C

ASTM D3029

J

1

Non notched cantilever beam impact

23°C

ASTM D4812

J/m

3

Dart impact equipped with measuring instruments

23°C, Energy at Peak

ASTM D3763

J

6

transmissivity

2540 µm

ASTM D1003

%

8

Haze

2540 µm

ASTM D1003

%

1