Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF503R-701 SABIC INNOVATIVE SHANGHAI
LEXAN™
fibre
High impact resistance、High rigidity、Glass fiber reinforced、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SHANGHAI/HF503R-701
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
2
Shrinkage rate
MD：3.20mm
内部方法
%
0
Specific volume
ASTMD792
cm³/g
0
Water absorption rate
平衡,23°C
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SHANGHAI/HF503R-701
Tensile strength 1
断裂
ASTMD638
Mpa
5
Elongation rate 2
断裂
ASTMD638
%
1
Bending modulus 3
50.0mm跨距
ASTMD790
Mpa
3
Bending strength 4
屈服,50.0mm跨距
ASTMD790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SHANGHAI/HF503R-701
thermal conductivity
ASTMC177
W/m/K
0
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
1
Vicat softening temperature
ASTMD15257
°C
1
Linear coefficient of thermal expansion
MD：-40到95°C
ASTME831
cm/cm/°C
3
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SHANGHAI/HF503R-701
Dielectric strength
3.20mm,inAir
ASTMD149
KV/mm
1
Volume resistivity
ASTMD257
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE SHANGHAI/HF503R-701
23°C
ASTMD256
J/m
1
23°C6
ISO180/1A
kJ/m²
1
-30°C5
ISO180/1A
kJ/m²
9
Cantilever beam without notch impact strength
23°C
ASTMD4812
J/m
2