PBT HR5315HFS NC010 DUPONT USA
Cristin®
Electronic and Electrical、Automotive components
High mobility、Easy to form、Easy to process
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/DUPONT USA/HR5315HFS NC010
Melt volume flow rate
250°C/2.16kg
ISO1133
cm3/10min
1
Melt viscosity
250°C,1000sec^-1
ISO11443
mPa·s
1
Shrinkage rate
TD
ISO294-4
%
1
Shrinkage rate
MD
ISO294-4
%
0
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
0
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/DUPONT USA/HR5315HFS NC010
Tensile modulus
ISO527-2
Mpa
5
Tensile strain
断裂
ISO527-2
%
3
Tensile stress
断裂
ISO527-2
Mpa
1
Bending stress
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PBT/DUPONT USA/HR5315HFS NC010
Glass transition temperature 3
ISO11357-2
°C
6
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature 5
ISO11357-3
°C
2
Electrical performance
Test Condition
Test Method
Unit
PBT/DUPONT USA/HR5315HFS NC010
Surface resistivity
IEC60093
ohms
1
Dielectric strength
IEC60243-1
KV/mm
4
Leakage Trace Index
IEC60112
V
6
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PBT/DUPONT USA/HR5315HFS NC010
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
3
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
6
flammability
Test Condition
Test Method
Unit
PBT/DUPONT USA/HR5315HFS NC010
Extreme Oxygen Index
ISO4589-2
%
2
Burning rate 4
1.00mm
ISO3795
mm/min
3