Melt mass flow rate

300°C/1.2kg

ASTMD1238

g/10min

8

Shrinkage rate

MD

ASTMD955

%

0

Water absorption rate

23°C,24hr

ASTMD570

%

0

Water absorption rate

平衡,23°C,50%RH

ASTMD570

%

0

Tensile strength

断裂

ASTMD638

Mpa

7

Tensile strength 2

屈服,23°C

ASTMD638

Mpa

6

Tensile modulus

ASTMD638

Mpa

2

Wear resistance - AngelinHaze3

Kg/m

%

4

elongation

屈服

ASTMD638

%

6

elongation

断裂

ASTMD638

%

1

Bending modulus

ASTMD790

Mpa

2

bending strength

ASTMD790

Mpa

9

Ball pressure temperature

IEC60598-1

°C

>

Hot deformation temperature

0.45MPa,Annealed,4.00mm

ASTMD648

°C

1

Hot deformation temperature

1.8MPa,Unannealed,4.00mm

ASTMD648

°C

1

Hot deformation temperature

1.8MPa,Annealed,4.00mm

ASTMD648

°C

1

Vicat softening temperature

ASTMD15256

°C

1

Linear coefficient of thermal expansion

MD：-40到82°C

ASTMD696

cm/cm/°C

6

Dielectric strength

ASTMD149

KV/mm

1

Leakage Trace Index

2.00mm

IEC60112

V

2

Volume resistivity

23°C

ASTMD257

ohms·cm

2

Suspended wall beam gap impact strength 4

23°C,3.20mm

ASTMD256

J/m

9

Dart impact with measuring instruments 5

23°C,3.20mm,TotalEnergy

ASTMD3763

J

8

Extreme Oxygen Index

ASTMD2863

%

2

Average degree of combustion

ASTMD635

CM

3

Hot filament ignition temperature 7

2.0mm

IEC60695-2-13

°C

8

transmissivity

ASTMD1003

%

8

Haze

ASTMD1003

%

0