Melt flow rate

230°C/3.8 kg

ASTM D1238

g/10 min

5

Melt flow rate

220°C/10.0 kg

ISO 1133

g/10 min

1

Shrinkage rate - flow

3.20 mm

内部方法

%

0

Tensile strength

屈服 2

ASTM D638

Mpa

4

Tensile strength

屈服

ISO 527-2/50

Mpa

4

Tensile strength

断裂 2

ASTM D638

Mpa

3

Tensile strength

断裂

ISO 527-2/50

Mpa

3

Tensile modulus

-- 1

ASTM D638

Mpa

2

Tensile modulus

--

ISO 527-2/1

Mpa

2

elongation

屈服 2

ASTM D638

%

2

elongation

屈服

ISO 527-2/50

%

2

elongation

断裂 2

ASTM D638

%

2

elongation

断裂

ISO 527-2/50

%

2

Bending modulus

50.0 mm 跨距 3

ASTM D790

Mpa

2

Bending modulus

-- 4

ISO 178

Mpa

2

Bending stress

-- 4, 5

ISO 178

Mpa

7

Bending stress

屈服, 50.0 mm 跨距 3

ASTM D790

Mpa

7

RTI

UL 746

°C

6

RTI Elec

UL 746

°C

6

RTI Imp

UL 746

°C

6

Vicat softening temperature

--

ISO 306/B50

°C

9

Vicat softening temperature

--

ISO 306/B120

°C

1

Linear coefficient of thermal expansion

流动 : -40 到 40°C

ASTM E831

cm/cm/°C

8

Linear coefficient of thermal expansion

横向 : -40 到 40°C

ASTM E831

cm/cm/°C

8

Thermal deformation temperature under load

0.45 MPa, 未退火, 3.20 mm

ASTM D648

°C

9

Thermal deformation temperature under load

1.8 MPa, 未退火, 3.20 mm

ASTM D648

°C

8

Thermal deformation temperature under load

1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7

ISO 75-2/Af

°C

8

Melt viscosity

240°C, 1000 sec^-1

ASTM D3835

Pa·s

2

Impact strength of simply supported beam gap 6

-30°C

ISO 179/1eA

kJ/m²

9

Impact strength of simply supported beam gap 6

23°C

ISO 179/1eA

kJ/m²

2

Dart impact equipped with measuring instruments

23°C, Total Energy

ASTM D3763

J

3