Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HIPS PH-88 BK TAIWAN CHIMEI
POLYREX®
Electrical field、Electronic field、Household goods、Plastic toy
High impact resistance、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
HIPS/TAIWAN CHIMEI/PH-88 BK
Density/specific gravity
--3
ASTMD792
g/cm³
1
Density/specific gravity
23°C
ISO1183
g/cm³
1
Melt volume flow rate
200°C/5.0kg
ISO1133
cm3/10min
5
Melt mass flow rate
200°C/5.0kg
ASTMD1238
g/10min
6
Shrinkage rate
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
HIPS/TAIWAN CHIMEI/PH-88 BK
Tensile stress
屈服
ISO527-2/50
Mpa
2
Tensile stress
断裂4
ASTMD638
Mpa
2
Tensile stress
断裂
ISO527-2/50
Mpa
2
elongation
断裂4
ASTMD638
%
4
elongation
断裂
ISO527-2/50
%
4
Bending modulus
--5
ASTMD790
Mpa
1
Bending modulus
--6
ISO178
Mpa
2
bending strength
--5
ASTMD790
Mpa
3
bending strength
--6
ISO178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
HIPS/TAIWAN CHIMEI/PH-88 BK
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
7
Hot deformation temperature
1.8MPa,退火
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,退火
ISO75-2/A
°C
8
Vicat softening temperature
--
ASTMD15257
°C
9
Vicat softening temperature
--
ISO306/A50
°C
9
Vicat softening temperature
--
ISO306/B50
°C
9
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
4
Impact performance
Test Condition
Test Method
Unit
HIPS/TAIWAN CHIMEI/PH-88 BK
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
6
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
1
Impact strength of cantilever beam gap
23°C,3.20mm
ASTMD256
J/m
9
Impact strength of cantilever beam gap
23°C,6.40mm
ASTMD256
J/m
8
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
6
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1