Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA/MXD6 1002H MITSUBISHI ENGINEERING JAPAN
RENY™
Electronic and Electrical、Automotive sector
High rigidity、High impact、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/1002H
Melt volume flow rate
275°C/2.16kg
ISO1133
cm3/10min
3
Melt mass flow rate
275°C/2.16kg
ISO1133
g/10min
4
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/1002H
Tensile modulus
ISO527-2
Mpa
1
Tensile strain
断裂
ISO527-2
%
1
Tensile stress
断裂
ISO527-2
Mpa
1
Bending modulus
ISO178
Mpa
1
Bending stress
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/1002H
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
5
Electrical performance
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/1002H
Surface resistivity
IEC60093
ohms
7
Dielectric strength
1.00mm
IEC60243-1
KV/mm
3
Dielectric strength
2.00mm
IEC60243-1
KV/mm
2
Leakage Trace Index
IEC60112
V
5
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PA/MXD6/MITSUBISHI ENGINEERING JAPAN/1002H
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
3