Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO/PA GTX918W-71967 SABIC INNOVATIVE US
NORYL GTX™
Electronic communication、household electrical appl、Automotive interior parts
Aging resistance、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/PA/SABIC INNOVATIVE US/GTX918W-71967
Melt flow rate
280°C/5.0 kg
ASTM D1238
g/10 min
4
Molten Volume Flow Rate (MVR)
280°C/1.2 kg
ISO 1133
cm3/10min
5
Shrinkage rate
流动 : 3.20 mm
内部方法
%
1
Shrinkage rate
横向流动 : 3.20 mm
内部方法
%
1
Water absorption rate
饱和, 23°C
ASTM D570
%
4
Mechanical performance
Test Condition
Test Method
Unit
PPO/PA/SABIC INNOVATIVE US/GTX918W-71967
Tensile strength
屈服 3
ASTM D638
Mpa
6
Tensile strength
屈服
ISO 527-2/50
Mpa
6
Tensile strength
断裂 3
ASTM D638
Mpa
5
Tensile strength
断裂
ISO 527-2/50
Mpa
5
Tensile modulus 2
ASTM D638
Mpa
8
elongation
屈服 3
ASTM D638
%
1
elongation
屈服
ISO 527-2/50
%
4
elongation
断裂 3
ASTM D638
%
5
elongation
断裂
ISO 527-2/50
%
3
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending modulus
-- 5
ISO 178
Mpa
2
Bending stress
-- 5, 6
ISO 178
Mpa
8
Bending stress
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PPO/PA/SABIC INNOVATIVE US/GTX918W-71967
thermal conductivity
ASTM C177
W/m/K
0
Vicat softening temperature
--
ASTM D152510
°C
2
Vicat softening temperature
--
ISO 306/A50
°C
2
Vicat softening temperature
--
ISO 306/B50
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
6
Linear coefficient of thermal expansion
流动 : 23 到 60°C
ISO 11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
6
Linear coefficient of thermal expansion
横向 : 23 到 60°C
ISO 11359-2
cm/cm/°C
8
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 9
ISO 75-2/Be
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Impact performance
Test Condition
Test Method
Unit
PPO/PA/SABIC INNOVATIVE US/GTX918W-71967
Impact strength of simply supported beam gap 7
-30°C
ISO 179/1eA
kJ/m²
1
Impact strength of simply supported beam gap 7
23°C
ISO 179/1eA
kJ/m²
2
Dart impact equipped with measuring instruments
23°C, Energy at Peak
ASTM D3763
J
4