Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 1150A64 JAPAN POLYPLASTIC
DURAFIDE®
Fiber grade
Low warpage、Glass fiber reinforced、Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1150A64
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1150A64
Fracture strain
ISO 527-1,2
%
1
Charpy Notched Impact Strength
ISO 179/1eA
KJ/m
5
tensile strength
ISO 527-1,2
Mpa
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Bending modulus
ISO 178
Mpa
1
bending strength
ISO 178
Mpa
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
1
Thermal performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1150A64
Load deformation temperature
1.8MPa
ISO 75-1
°C
2
Electrical performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1150A64
Surface resistivity
IEC 60093
Ω
3
Dielectric loss factor
3mmt
IEC 60243-1
KV/mm
1
Resistant to conductive tracks
IEC 60112
V
1
Volume resistivity
IEC 60093
Ω·cm
2
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
2
Basic performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1150A64
density
ISO 1183
g/cm
1
Melt viscosity
310℃、1000/sec
ISO 11443
Pa·s
2
Water absorption rate
23℃,水中24小时
ISO 62
%
0