PA66 MKD1016-FW9153 LOTTE KOREA
INFINO®
Electronic and electrical
Glass fiber reinforced、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/LOTTE KOREA/MKD1016-FW9153
Ash Content
--
ISO3451
%
5
Ash Content
--
ASTMD5630
%
5
Melt mass flow rate
275°C/2.16kg
ASTMD1238
g/10min
1
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
1
Melt mass flow rate
275°C/2.16kg
ISO1133
g/10min
1
Melt mass flow rate
300°C/1.2kg
ISO1133
g/10min
1
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD:3.20mm
ISO2577
%
0
Shrinkage rate
MD:3.20mm
ISO2577
%
0
Water absorption rate
平衡,23°C
ASTMD570
%
3
Water absorption rate
平衡,23°C,50%RH
ISO62
%
3
Mechanical performance
Test Condition
Test Method
Unit
PA66/LOTTE KOREA/MKD1016-FW9153
Tensile strength 2
屈服
ASTMD638
Mpa
2
Tensile strength 2
断裂
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/50
Mpa
1
Tensile modulus 2
ASTMD638
Mpa
1
Tensile strain
断裂
ISO527-2/5
%
4
Tensile stress
屈服
ISO527-2/5
Mpa
2
Tensile stress
断裂
ISO527-2/50
Mpa
2
Elongation rate 2
断裂
ASTMD638
%
4
Bending modulus 3
ASTMD790
Mpa
1
Bending modulus 4
ISO178
Mpa
1
Bending strength 3
ASTMD790
Mpa
3
Bending stress 4
ISO178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
PA66/LOTTE KOREA/MKD1016-FW9153
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
2
Impact performance
Test Condition
Test Method
Unit
PA66/LOTTE KOREA/MKD1016-FW9153
CharpyNotchedImpactStrength5
23°C
ISO179/1eA
kJ/m²
1
Suspended wall beam gap impact strength 5
23°C
ISO180/1A
kJ/m²
1