Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A504FG1 TORAY JAPAN
Torelina®
Automotive Applications、sporting goods
Glass fiber reinforced、enhance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PPS/TORAY JAPAN/A504FG1
Molding shrinkage rate
ASTM D955
%
0
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
PPS/TORAY JAPAN/A504FG1
Shrinkage rate
TD:3.00mm2
内部方法
%
0
Shrinkage rate
MD:3.00mm4
内部方法
%
0
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/TORAY JAPAN/A504FG1
elongation at break
ASTM D638/ISO 527
%
1
shear strength
23°C
JISK7214
Mpa
7
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Tensile strain
断裂,23°C
ISO527-2
%
1
Tensile stress
屈服,23°C
ISO527-2
Mpa
1
Taber abraser
1000Cycles
ISO9352
mg
5
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Bending modulus
23°C
ISO178
Mpa
1
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
Bending stress
23°C
ISO178
Mpa
2
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
3
Thermal performance
Test Condition
Test Method
Unit
PPS/TORAY JAPAN/A504FG1
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
>
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature
ISO11357-3
°C
2
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
3
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
1
Electrical performance
Test Condition
Test Method
Unit
PPS/TORAY JAPAN/A504FG1
Dielectric strength
IEC60243-1
KV/mm
2
Volume resistivity
IEC60093
ohms·cm
1
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
1
Impact performance
Test Condition
Test Method
Unit
PPS/TORAY JAPAN/A504FG1
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
3
Supplementary Information
Test Condition
Test Method
Unit
PPS/TORAY JAPAN/A504FG1
BarFlowLength6
320°C,1.00mm
内部方法
mm
2