Density/specific gravity

ASTMD792

g/cm³

1

Density/specific gravity

ISO11832

kg/m3

1

Melt volume flow rate

260°C/5.0kg

ISO11332

cm3/10min

1

Melt mass flow rate

250°C/2.16kg

ASTMD1238

g/10min

5

Shrinkage rate

MD：3.20mm,InjectionMolded

ASTMD955

%

0

Water absorption rate

饱和

ISO622

%

0

Nominal strainatbreak

ISO527-22

%

>

Tensile strength 2

屈服,3.20mm,注塑

ASTMD638

Mpa

5

Tensile modulus

ISO527-22

Mpa

2

Tensile strain

屈服

ISO527-22

%

4

Tensile strain 3

Break,3.20mm,InjectionMolded

ASTMD638

%

>

Tensile stress

屈服

ISO527-22

Mpa

6

Bending modulus 4

3.20mm,InjectionMolded

ASTMD790

Mpa

2

Bending strength 4

3.20mm

ASTMD790

Mpa

7

RTIElec

1.6mm

UL746

°C

6

RTIElec

3.0mm

UL746

°C

6

Evolution Calendar intelligent importer

1.6mm

UL746

°C

6

Evolution Calendar intelligent importer

3.0mm

UL746

°C

6

RTIStr

1.6mm

UL746

°C

6

RTIStr

3.0mm

UL746

°C

6

Glass transition temperature 9

ISO11357-22

°C

1

Hot deformation temperature

1.8MPa,Unannealed,6.40mm,InjectionMolded

ASTMD648

°C

1

Hot deformation temperature

1.8MPa

ISO75-22

°C

1

Vicat softening temperature

50N

ISO3062

°C

1

Linear coefficient of thermal expansion

MD

ISO11359-22

cm/cm/°C

7

Linear coefficient of thermal expansion

TD

ISO11359-22

cm/cm/°C

8

Electrical strength

IEC60243-12

KV/mm

4

Surface resistivity

IEC600932

ohms

3

Volume resistivity

IEC600932

ohms·m

>

Charpy Notched Impact Strength

-30°C

ISO179/1eA2

kJ/m²

3

Impact strength of cantilever beam gap

-30°C,3.20mm,注塑

ASTMD256

J/m

4

Impact strength of cantilever beam gap

23°C,3.20mm,注塑

ASTMD256

J/m

6