Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
AES KD100W UMG JAPAN
DIALAC®
--
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
AES/UMG JAPAN/KD100W
Dissolved volume flow rate
220℃/2.16 kg
ISO 1133
cm3/10min
9
Melt volume flow rate
220°C/10.0kg
ISO1133
cm3/10min
9
Shrinkage rate
MD：23°C
ISO294-4
%
0
Shrinkage rate
MD，23℃
ISO 294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
AES/UMG JAPAN/KD100W
Charpy Notched Impact Strength
-30℃
ISO 179
kJ/m²
2
Tensile modulus
23℃
ISO 527-2
Mpa
2
Tensile modulus
23°C
ISO527-2
Mpa
2
Tensile stress
23°C
ISO527-2
Mpa
4
Tensile stress
23℃
ISO 527-2
Mpa
4
Rockwell hardness
23℃
ISO 2039-2
R 计秤
1
Bending modulus
23℃
ISO 178
Mpa
2
Bending modulus 2
23°C
ISO178
Mpa
2
bending strength
23℃
ISO 178
Mpa
6
Bending stress 2
23°C
ISO178
Mpa
6
Thermal performance
Test Condition
Test Method
Unit
AES/UMG JAPAN/KD100W
Hot deformation temperature
1.80MPa，未退火
ISO 75-2/Af
°C
7
Hot deformation temperature
1.8MPa,未退火
ISO75-2/Af
°C
7
Linear expansion coefficient
流动
ISO 11359-2
cm/cm/℃
0
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
8