Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI ATX3562R-7301 SABIC INNOVATIVE US
ULTEM™
Electronic and electrical、Automotive components
Thermal stability、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/ATX3562R-7301
Melt volume flow rate
360°C/5.0kg
ISO1133
cm3/10min
2
Melt mass flow rate
337°C/6.6kg
ASTMD1238
g/10min
2
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/ATX3562R-7301
Tensile strength 3
屈服
ASTMD638
Mpa
1
Tensile strength 3
断裂
ASTMD638
Mpa
1
Tensile modulus
ISO527-2/1
Mpa
1
Tensile modulus 2
ASTMD638
Mpa
1
Tensile strain
屈服
ISO527-2/5
%
1
Tensile strain
断裂
ISO527-2/5
%
1
Tensile stress
断裂
ISO527-2/5
Mpa
1
Tensile stress
屈服
ISO527-2/5
Mpa
1
Elongation rate 3
屈服
ASTMD638
%
2
Elongation rate 4
断裂
ASTMD638
%
2
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
1
Bending modulus 5
ISO178
Mpa
1
Bending strength 4
屈服,50.0mm跨距
ASTMD790
Mpa
1
Bending strength 5,6
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/ATX3562R-7301
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 9
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
1
Hot deformation temperature 9
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
1
Vicat softening temperature
ASTMD152510
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40to150°C
ASTME831
cm/cm/°C
1
Linear coefficient of thermal expansion
MD：23到150°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：-40to150°C
ASTME831
cm/cm/°C
3
Linear coefficient of thermal expansion
TD：23to150°C
ISO11359-2
cm/cm/°C
3
Electrical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/ATX3562R-7301
Surface resistivity
ASTMD257
ohms
2
Volume resistivity
ASTMD257
ohms·cm
6
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/ATX3562R-7301
ReverseNotchIzodImpact
3.20mm
ASTMD256
J/m
1
UnnotchedIzodImpactStrength8
23°C
ISO180/1U
kJ/m²
5
Impact strength of simply supported beam gap 7
23°C
ISO179/1eA
kJ/m²
4
Suspended wall beam gap impact strength 8
-30°C
ISO180/1A
kJ/m²
5
Suspended wall beam gap impact strength 8
23°C
ISO180/1A
kJ/m²
5
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
1