Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT/PC 357U-1001 SABIC INNOVATIVE SHANGHAI
VALOX™
Roller、switch、Shell
UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/PC/SABIC INNOVATIVE SHANGHAI/357U-1001
Melt volume flow rate
250°C/5.0kg
ISO1133
cm3/10min
8
Shrinkage rate
MD3
内部方法
%
1
Shrinkage rate
MD4
内部方法
%
0
Shrinkage rate
TD3
内部方法
%
1
Shrinkage rate
TD4
内部方法
%
0
Specific volume
ASTMD792
cm³/g
0
Water absorption rate
24hr
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/PC/SABIC INNOVATIVE SHANGHAI/357U-1001
Tensile strength 5
屈服
ASTMD638
Mpa
4
Tensile strength 5
断裂
ASTMD638
Mpa
4
Elongation rate 5
断裂
ASTMD638
%
1
Bending modulus 6
50.0mm跨距
ASTMD790
Mpa
2
Bending strength 6
屈服,50.0mm跨距
ASTMD790
Mpa
8
Bending strength 6
断裂,50.0mm跨距
ASTMD790
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PBT/PC/SABIC INNOVATIVE SHANGHAI/357U-1001
RTI
UL746
°C
1
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
9
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
9
Linear coefficient of thermal expansion
MD：60到138°C
ASTME831
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PBT/PC/SABIC INNOVATIVE SHANGHAI/357U-1001
Dielectric strength
3.20mm,inOil
ASTMD149
KV/mm
1
Dielectric strength
1.60mm,inOil
ASTMD149
KV/mm
2
Dielectric strength
3.20mm,inAir
ASTMD149
KV/mm
1
Volume resistivity
ASTMD257
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PBT/PC/SABIC INNOVATIVE SHANGHAI/357U-1001
Falling hammer impact
23°C7
ASTMD3029
J
4
Falling hammer impact
23°C
ASTMD3029
J
4
Cantilever beam without notch impact strength
23°C
ASTMD4812
J/m
3
flammability
Test Condition
Test Method
Unit
PBT/PC/SABIC INNOVATIVE SHANGHAI/357U-1001
Extreme Oxygen Index
ASTMD2863
%
3