Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPU 1185A HEADWAY TAIWAN
--
--
Filler, mineral filler, 3
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
TPU/HEADWAY TAIWAN/1185A
density
ISO1183
g/cm³
1
Melt mass flow rate
230°C/2.16kg
ISO1133
g/10min
5
Shrinkage rate
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
TPU/HEADWAY TAIWAN/1185A
Tensile modulus
1.00mm
ISO527-2
Mpa
2
Tensile strain
屈服
ISO527-2/50
%
3
Tensile stress
屈服
ISO527-2/50
Mpa
2
Bending modulus
ISO178
Mpa
3
Bending stress
ISO178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
TPU/HEADWAY TAIWAN/1185A
MeltEnergy
ISO11357
kJ/kg
6
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Vicat softening temperature
--
ISO306/A
°C
1
Vicat softening temperature
--
ISO306/B
°C
7
Impact performance
Test Condition
Test Method
Unit
TPU/HEADWAY TAIWAN/1185A
Charpy Notched Impact Strength
-20°C
ISO179/1eA
kJ/m²
2
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
7
Impact strength of simply supported beam without notch
-20°C
ISO179/1eU
kJ/m²
2
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
6
Unscented Izod impact strength
-20°C
ISO180/1U
kJ/m²
2
Unscented Izod impact strength
23°C
ISO180/1U
kJ/m²
7
Impact strength of cantilever beam gap
-20°C
ISO180/1A
kJ/m²
3
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
9
hardness
Test Condition
Test Method
Unit
TPU/HEADWAY TAIWAN/1185A
Ball pressure hardness
H358/30
ISO2039-1
Mpa
5
flammability
Test Condition
Test Method
Unit
TPU/HEADWAY TAIWAN/1185A
atomization
DIN75201
mg
<
Supplementary Information
Test Condition
Test Method
Unit
TPU/HEADWAY TAIWAN/1185A
Emission
VDA277
µgC/g
<