Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 6 GF15 A SCHULMAN USA
SCHULAMID®
--
Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/A SCHULMAN USA/6 GF15
Stickiness number
ISO307
cm³/g
1
Mechanical performance
Test Condition
Test Method
Unit
PA6/A SCHULMAN USA/6 GF15
Tensile modulus
ISO527-2/1A/1
Mpa
5
Tensile strain
断裂
ISO527-2/1A/5
%
3
Tensile stress
断裂
ISO527-2/1A/5
Mpa
1
Bending modulus 2
ISO178
Mpa
4
Bending strain
ISO178
%
6
Bending stress 2
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PA6/A SCHULMAN USA/6 GF15
Hot deformation temperature
0.45MPa,未退火
ISO75-2/Bf
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/Af
°C
2
Vicat softening temperature
--
ISO306/A50
°C
2
Vicat softening temperature
--
ISO306/B50
°C
2
Impact performance
Test Condition
Test Method
Unit
PA6/A SCHULMAN USA/6 GF15
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
4
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
4
hardness
Test Condition
Test Method
Unit
PA6/A SCHULMAN USA/6 GF15
Ball pressure hardness
H358/30
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PA6/A SCHULMAN USA/6 GF15
Burning rate
ISO3795
mm/min
<
Burning wire flammability index
1.5mm
IEC60695-2-12
°C
-
Burning wire flammability index
3.0mm
IEC60695-2-12
°C
-