PC/ABS CY4000M-7M2D109 SABIC INNOVATIVE NANSHA
CYCOLOY™
Electronic and electrical、Shell
high strength、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CY4000M-7M2D109
proportion
ASTM D792
g/cm³
1
Melt index
260℃ 2.16kg
ASTM D1238
g/10min
2
Shrinkage rate
流动3.2mm
ASTM D995
%
0
Shrinkage rate
垂直3.2mm
ASTM D995
%
0
Water absorption rate
23℃饱和
ISO 62
%
0
Water absorption rate
23℃ 50RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CY4000M-7M2D109
tensile strength
屈服23℃
ASTM D638
Mpa
6
tensile strength
23℃ 50mm/min
ASTM D638
Mpa
4
elongation
屈服23℃ 50mm/min
ASTM D638
%
4
elongation
23℃
ASTM D638
%
4
Bending modulus
23℃
ASTM D790
Mpa
2
bending strength
屈服23℃
ASTM D790
Mpa
9
Cantilever beam gap impact
-30℃
ASTM D256
J/m
1
Cantilever beam notch impact -30 ℃
23℃
ASTM D256
J/m
5
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CY4000M-7M2D109
Vertical expansion coefficient
ASTM D696
cm/cm/℃
0
Hot deformation temperature
未退火1.8MPa
ASTM D648
°C
8
Vicat softening temperature
ASTM DI525
°C
9
Vicat softening temperature
50℃/hr 50N
ISO 306
°C
9
Vicat softening temperature
120℃/hr 50N
ISO 306
°C
1