density

ASTMD792

g/cm³

1

density

ISO1183

g/cm³

1

Melt Volume-Flow Rate (MVR)

250°C/5.0kg

ISO1133

cm3/10min

2

Melt mass flow rate

250°C/5.0kg

ASTMD1238

g/10min

4

Shrinkage rate

MD：--2

内部方法

%

0

Shrinkage rate

MD：3.20mm

内部方法

%

0

Shrinkage rate

TD：--2

内部方法

%

0

Shrinkage rate

TD：3.20mm

内部方法

%

0

Specific volume

ASTMD792

cm³/g

0

Water absorption rate

饱和,23°C

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

FlexuralStrength

Break,50.0mmSpan

ASTMD790

Mpa

1

Impact strength of simply supported beam gap

-30°C

ISO179/1eA

kJ/m²

6

Impact strength of simply supported beam gap

23°C

ISO179/1eA

kJ/m²

7

The impact strength of a simply supported beam without a notch is

-30°C

ISO179/1eU

kJ/m²

5

The impact strength of a simply supported beam without a notch is

23°C

ISO179/1eU

kJ/m²

5

Tensile strength

屈服

ASTMD638

Mpa

1

Tensile modulus

ASTMD638

Mpa

1

Tensile modulus

ISO527-2/1

Mpa

1

tensile strength

屈服

ISO527-2/5

Mpa

1

tensile strength

Break

ASTMD638

Mpa

1

tensile strength

断裂

ISO527-2/5

Mpa

1

Ball pressure hardness

H358/30

ISO2039-1

Mpa

1

elongation

屈服

ASTMD638

%

2

elongation

屈服

ISO527-2/5

%

1

elongation

断裂

ASTMD638

%

2

elongation

断裂

ISO527-2/5

%

1

Taber abraser

1000Cycles,1000g,CS-17转轮

内部方法

mg

2

Bending modulus

ISO178

Mpa

9

Bending modulus

50.0mmSpan

ASTMD790

Mpa

9

bending strength

ISO178

Mpa

1

Unscented Izod Impact Strength

-30°C

ISO180/1U

kJ/m²

4

Unscented Izod Impact Strength

23°C

ISO180/1U

kJ/m²

4

Suspended wall beam gap impact strength

-30°C

ISO180/1A

kJ/m²

6

Suspended wall beam gap impact strength

23°C

ISO180/1A

kJ/m²

7

Impact strength of cantilever beam gap

23°C

ASTMD4812

J/m

6

Impact strength of cantilever beam gap

-30°C

ASTMD256

J/m

5

Impact strength of cantilever beam gap

23°C

ASTMD256

J/m

6

Dart impact equipped with measuring instruments

23°C,TotalEnergy

ASTMD3763

J

5

RTI Imp

UL746

°C

1

RTIElec

UL746

°C

1

RTIStr

UL746

°C

1

thermal conductivity

ISO8302

W/m/K

0

Hot deformation temperature

0.45MPa,未退火,3.20mm

ASTMD648

°C

2

Hot deformation temperature

0.45MPa,Unannealed,100mmSpan

ISO75-2/Be

°C

2

Hot deformation temperature

1.8MPa,未退火,3.20mm

ASTMD648

°C

2

Hot deformation temperature

1.8MPa,未退火,100mm跨距9

ISO75-2/Ae

°C

1

Hot deformation temperature

1.8MPa,未退火,64.0mm跨距10

ISO75-2/Af

°C

2

vicat softening point

ASTMD152511

°C

2

vicat softening point

--

ISO306/A50

°C

2

vicat softening point

--

ISO306/B50

°C

2

vicat softening point

--

ISO306/B120

°C

2

Linear coefficient of thermal expansion

MD：-40到40°C

ASTME831

cm/cm/°C

2

Linear coefficient of thermal expansion

MD：-40to40°C

ISO11359-2

cm/cm/°C

2

Linear coefficient of thermal expansion

MD：23到80°C

ISO11359-2

cm/cm/°C

2

Linear coefficient of thermal expansion

TD：-40到40°C

ASTME831

cm/cm/°C

8

Linear coefficient of thermal expansion

TD：-40to40°C

ISO11359-2

cm/cm/°C

8

Linear coefficient of thermal expansion

TD：23到80°C

ISO11359-2

cm/cm/°C

1

Surface resistivity

IEC60093

ohms

>

Dielectric strength

1.60mm,在油中

ASTMD149

KV/mm

2

Dielectric strength

3.20mm,inAir

ASTMD149

KV/mm

1

Dielectric strength

0.800mm,在油中

IEC60243-1

KV/mm

2

Dielectric strength

1.60mm,在油中

IEC60243-1

KV/mm

2

Dielectric strength

3.20mm,在油中

IEC60243-1

KV/mm

1

Leakage Trace Index

--

IEC60112

V

1

Leakage Trace Index

解决方案B

IEC60112

V

1

Volume resistivity

ASTMD257

ohms·cm

>

Volume resistivity

IEC60093

ohms·cm

>

Extreme Oxygen Index

ISO4589-2

%

3

Burning wire flammability index

1.0mm

IEC60695-2-12

°C

9