Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC D451-701 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
--
Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/D451-701
300°C/2.16kg
ISO1133
cm3/10min
1
300°C/5.0kg
ASTMD1238
cm3/10min
4
Melt mass flow rate
300°C/2.16kg
ASTMD1238
g/10min
1
Melt mass flow rate
300°C/5.0kg
ASTMD1238
g/10min
5
Shrinkage rate
MD:24小时
ASTMD955
%
0
Shrinkage rate
TD:24小时
ASTMD955
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/D451-701
Tensile strength 2
断裂
ASTMD638
Mpa
1
Tensile modulus 1
ASTMD638
Mpa
1
Elongation rate 3
断裂
ASTMD638
%
2
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
9
Bending strength 5
断裂,50.0mm跨距
ASTMD790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/D451-701
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831
cm/cm/°C
1
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831
cm/cm/°C
5
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/D451-701
Impact strength of simply supported beam gap 6
23°C
ISO179/1eA
kJ/m²
1
The impact strength of a simply supported beam without a notch is 7
23°C
ISO179/1eU
kJ/m²
3
Cantilever beam without notch impact strength
23°C
ASTMD4812
J/m
5