PBT RG301 BK SHINKONG TAIWAN
SHINITE®
Electronic and electrical、Automotive Applications、Automotive External Parts、Parts under the hood of a、Application in the automo
Carbon fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/SHINKONG TAIWAN/RG301 BK
density
ASTMD792
g/cm³
1
density
ISO1183
g/cm³
1
Melt mass flow rate
200°C/21.6kg
ASTMD1238
g/10min
1
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
8
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
8
Shrinkage rate
MD
ASTMD955
%
0
Shrinkage rate
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/SHINKONG TAIWAN/RG301 BK
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1
tensile strength
屈服
ASTMD638
Mpa
4
tensile strength
屈服
ISO527-2
Mpa
4
elongation
屈服
ASTMD638
%
2
elongation
断裂
ISO527-2
%
2
Bending modulus
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
ISO178
Mpa
7
bending strength
屈服
ASTMD790
Mpa
6
Impact strength of cantilever beam gap
23°C,3.20mm
ASTMD256
J/m
2
Impact strength of cantilever beam gap
23°C,6.40mm
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1
Thermal performance
Test Condition
Test Method
Unit
PBT/SHINKONG TAIWAN/RG301 BK
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
9
vicat softening point
ASTMD15252
°C
1
vicat softening point
ISO306/B50
°C
1