Apparent density 2

ISO60

g/cm³

0

Density/specific gravity

23°C

ISO1183

g/cm³

1

Melt volume flow rate

300°C/1.2kg

ISO1133

cm3/10min

1

Melt mass flow rate

300°C/1.2kg

ISO1133

g/10min

1

Shrinkage rate

TD

ISO2577

%

0

Shrinkage rate

MD

ISO2577

%

0

Shrinkage rate

TD:2.00mm3

ISO294-4

%

0

Shrinkage rate

MD:2.00mm3

ISO294-4

%

0

Water absorption rate

饱和,23°C

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

TensileCreepModule

1hr

ISO899-1

Mpa

2

Nominal tensile fracture strain

23°C

ISO527-2/50

%

>

Tensile modulus

23°C

ISO527-2/1

Mpa

2

Tensile creep modulus

1000hr

ISO899-1

Mpa

1

Tensile strain

屈服,23°C

ISO527-2/50

%

6

Tensile strain

断裂,23°C

ISO527-2/50

%

1

Tensile stress

屈服,23°C

ISO527-2/50

Mpa

6

Tensile stress

断裂,23°C

ISO527-2/50

Mpa

7

Bending modulus 4

23°C

ISO178

Mpa

2

Bending strain 5

23°C

ISO178

%

7

Bending stress 4

23°C

ISO178

Mpa

9

Bending stress 4

3.5%Strain,23°C

ISO178

Mpa

7

RTIElec

1.5mm

UL746

°C

1

Evolution Calendar intelligent importer

1.5mm

UL746

°C

1

RTIStr

1.5mm

UL746

°C

1

Glass transition temperature 8

ISO11357-2

°C

1

Thermal conductivity coefficient 9

23°C

ISO8302

W/m/K

0

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

1

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

1

Vicat softening temperature

--

ISO306/B120

°C

1

Vicat softening temperature

--

ISO306/B50

°C

1

Linear coefficient of thermal expansion

TD：23to55°C

ISO11359-2

cm/cm/°C

6

Linear coefficient of thermal expansion

MD：23到55°C

ISO11359-2

cm/cm/°C

6

Surface resistivity

IEC60093

ohms

1

Dielectric strength

23°C,1.00mm

IEC60243-1

KV/mm

3

Leakage Trace Index

解决方案A

IEC60112

V

2

Leakage Trace Index

解决方案B

IEC60112

V

1

Volume resistivity

23°C

IEC60093

ohms·cm

1

GasPermeation

CarbonDioxide:23°C,25.4µm

ISO2556

cm³/m²/bar/24hr

1

GasPermeation

CarbonDioxide:23°C,100.0µm

ISO2556

cm³/m²/bar/24hr

4

GasPermeation

Nitrogen:23°C,25.4µm

ISO2556

cm³/m²/bar/24hr

5

GasPermeation

Nitrogen:23°C,100.0µm

ISO2556

cm³/m²/bar/24hr

1

GasPermeation

Oxygen:23°C,25.4µm

ISO2556

cm³/m²/bar/24hr

2

GasPermeation

Oxygen:23°C,100.0µm

ISO2556

cm³/m²/bar/24hr

7

WaterVaporTransmission Rate

23°C,85%RH,100µm

ISO15106-1

g/m²/24hr

1

Multi axis Instrumented Peak Impact Force

-30°C

ISO6603-2

N

6

Multi axis Instrumented Peak Impact Force

23°C

ISO6603-2

N

5

Multi axis Instrumented Impact Energy

-30°C

ISO6603-2

J

6

Multi axis Instrumented Impact Energy

23°C

ISO6603-2

J

6

Impact strength of simply supported beam gap 6

-30°C,完全断裂

ISO7391

kJ/m²

1

Impact strength of simply supported beam gap 6

23°C,局部断裂

ISO7391

kJ/m²

7

Suspended wall beam gap impact strength 7

-30°C,完全断裂

ISO7391

kJ/m²

1

Suspended wall beam gap impact strength 7

23°C,局部断裂

ISO7391

kJ/m²

6

Ball pressure hardness

ISO2039-1

Mpa

1

FlashIgnitionTemperature

ASTMD1929

°C

4

GlowWireTest

1.50mm

EDFHN60E.02

°C

7

GlowWireTest

3.00mm

EDFHN60E.02

°C

7

SelfIgnition

ASTMD1929

°C

5

Extreme Oxygen Index 10

ISO4589-2

%

3

Hot filament ignition temperature

3.0mm

IEC60695-2-13

°C

8

Hot filament ignition temperature

0.75mm

IEC60695-2-13

°C

8

Hot filament ignition temperature

1.5mm

IEC60695-2-13

°C

8

Needle flame test

MethodK:3.00mm

IEC60695-11-5

min

2

Needle flame test

MethodK:2.00mm

IEC60695-11-5

min

2

Needle flame test

MethodF:1.50mm

IEC60695-11-5

min

2

Needle flame test

MethodF:2.00mm

IEC60695-11-5

min

2

Needle flame test

MethodF:3.00mm

IEC60695-11-5

min

2

Needle flame test

MethodK:1.50mm

IEC60695-11-5

min

1

Burning wire flammability index

0.75mm

IEC60695-2-12

°C

8

Burning wire flammability index

1.5mm

IEC60695-2-12

°C

9

Burning wire flammability index

3.0mm

IEC60695-2-12

°C

9

transmissivity

1000µm

ISO13468-2

%

8

transmissivity

2000µm

ISO13468-2

%

8

transmissivity

3000µm

ISO13468-2

%

8

transmissivity

4000µm

ISO13468-2

%

8