density

23°C

ISO 1183

g/cm³

1

Melt flow rate

330°C/2.16 kg

ISO 1133

g/10 min

8

Molten Volume Flow Rate (MVR)

330°C/2.16 kg

ISO 1133

cm3/10min

8

Shrinkage rate 3

横向流量 : 2.00 mm

ISO 294-4

%

0

Shrinkage rate 3

流量 : 2.00 mm

ISO 294-4

%

0

Water absorption rate

饱和, 23°C

ISO 62

%

0

Water absorption rate

平衡, 23°C, 50% RH

ISO 62

%

0

Nominal tensile fracture strain

23°C

ISO 527-2/50

%

>

Tensile modulus

23°C

ISO 527-2/1

Mpa

2

Tensile strain

屈服, 23°C

ISO 527-2/50

%

6

Tensile stress

屈服, 23°C

ISO 527-2/50

Mpa

7

Bending modulus

23°C

ISO 178

Mpa

2

Bending stress

23°C

ISO 178

Mpa

1

RTI

UL 746

°C

1

RTI Elec

UL 746

°C

1

RTI Imp

UL 746

°C

1

Hot deformation temperature

0.45 MPa, 未退火

ISO 75-2/B

°C

1

Hot deformation temperature

1.8 MPa, 未退火

ISO 75-2/A

°C

1

Vicat softening temperature

ISO 306/B120

°C

2

Linear coefficient of thermal expansion

流动 : 23 到 55°C

ISO 11359-2

cm/cm/°C

6

Linear coefficient of thermal expansion

横向 : 23 到 55°C

ISO 11359-2

cm/cm/°C

6

Surface resistivity

IEC 60093

ohms

1

Dielectric strength

23°C, 1.00 mm

IEC 60243-1

KV/mm

3

Leakage Trace Index

解决方案 A

IEC 60112

V

6

Leakage Trace Index

解决方案 B

IEC 60112

V

1

Volume resistivity

23°C

IEC 60093

ohms·cm

1

Ball pressure hardness

ISO 2039-1

Mpa

1

Extreme Oxygen Index 5

ISO 4589-2

%

2

Burning wire flammability index

IEC 60695-2-12

°C

8

transmissivity

1000 µm

ISO 13468-2

%

8