Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP L304M50 TORAY JAPAN
SIVERAS™
Electrical components、Electrical appliances
enhance、Glass fiber reinforced、High toughness、High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
LCP/TORAY JAPAN/L304M50
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
LCP/TORAY JAPAN/L304M50
Shrinkage rate
MD
ASTM D955
%
0
Shrinkage rate
TD
ASTM D955
%
0
Water absorption rate
24 hr
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
LCP/TORAY JAPAN/L304M50
Tensile strength
ASTM D638
Mpa
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
elongation
ASTM D638/ISO 527
%
2
elongation
断裂
ASTM D1708
%
2
Bending modulus
ASTM D790
Mpa
1
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
bending strength
ASTM D790
Mpa
1
Cantilever beam without notch impact strength
ASTM D256
J/m
6
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
6
Thermal performance
Test Condition
Test Method
Unit
LCP/TORAY JAPAN/L304M50
Hot deformation temperature
1.8 MPa, 未退火
ASTM D648
°C
2
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Linear expansion coefficient
流动
ASTM D696
cm/cm/℃
0
Linear expansion coefficient
横向
ASTM D696
cm/cm/℃
0
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
1
Electrical performance
Test Condition
Test Method
Unit
LCP/TORAY JAPAN/L304M50
Dielectric strength
ASTM D149
KV/mm
5
Arc resistance
ASTM D495
sec
1