PBT VX5011 SABIC INNOVATIVE US
VALOX™
packing、Electronic and Electrical
Low warpage、Aging resistance、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5011
Density/specific gravity
ASTMD792,ISO1183
g/cm³
1
Melt volume flow rate
250°C/2.16kg
ISO1133
cm3/10min
1
Melt volume flow rate
250°C/5.0kg
ISO1133
cm3/10min
5
Melt volume flow rate
265°C/5.0kg
ISO1133
cm3/10min
7
Melt mass flow rate
265°C/5.0kg
ASTMD1238
g/10min
8
Melt mass flow rate
266°C/5.0kg
ASTMD1238
g/10min
8
Melt mass flow rate
200°C/3.8kg
ASTMD1238
g/10min
1
Shrinkage rate
MD1
内部方法
%
0
Shrinkage rate
MD:3.20mm
内部方法
%
0
Shrinkage rate
TD2
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5011
--
ISO527-2/1
Mpa
4
--10
ISO178
Mpa
1
--11
ISO178
Mpa
1
--3
ASTMD638
Mpa
4
50.0mm span 8
ASTMD790
Mpa
3
--9
ISO178
Mpa
4
crack
ISO527-2/5
%
3
crack
ISO527-2/5
Mpa
9
Fracture 5
ASTMD638
Mpa
9
Fracture 7
ASTMD638
%
3
Fracture bending strain 13
ISO178
%
5
yield
ISO527-2/5
Mpa
9
yield
ISO527-2/5
%
3
Yield, 50.0mm span 12
ASTMD790
Mpa
1
Surrender 4
ASTMD638
Mpa
9
Surrender 6
ASTMD638
%
3
Taber abraser
1000Cycles,1000g,CS-17转轮
内部方法
mg
5
Thermal performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5011
--
ASTMD1525,ISO306/B50,ISO306/B12025
°C
1
--
ASTMD1525,ISO306/A501426
°C
2
0.45MPa, unannealed, 3.20mm
ASTMD648
°C
1
0.45MPa, unannealed, 64.0mm span 23
ISO75-2/Bf
°C
1
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
1
1.8MPa, unannealed, 64.0mm span 24
ISO75-2/Af
°C
1
Horizontal: 23 to 150 ° C
ISO11359-2
cm/cm/°C
1
Horizontal: 23 to 80 ° C
ISO11359-2
cm/cm/°C
9
Horizontal: -40 to 40 ° C
ASTME831
cm/cm/°C
9
Horizontal: -40 to 40 ° C
ISO11359-2
cm/cm/°C
7
Flow: 23 to 150 ° C
ISO11359-2
cm/cm/°C
3
Flow: 23 to 80 ° C
ISO11359-2
cm/cm/°C
4
Flow: -40 to 40 ° C
ASTME831
cm/cm/°C
4
Flow: -40 to 40 ° C
ISO11359-2
cm/cm/°C
3
Electrical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5011
0.800mm,inOil
ASTMD149
KV/mm
2
0.800mm, in oil
IEC60243-1
KV/mm
2
1.60mm,inOil
ASTMD149
KV/mm
2
1.60mm, in oil
IEC60243-1
KV/mm
2
3.20mm, inoil
ASTMD149
KV/mm
1
3.20mm, in oil
IEC60243-1
KV/mm
1
Surface resistivity
IEC60093
ohms
>
Leakage Trace Index
--
IEC60112
V
2
Leakage Trace Index
解决方案B
IEC60112
V
1
Volume resistivity
ASTMD257,IEC60093
ohms·cm
>
Filling analysis
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5011
Melt viscosity
260°C,1500sec^-1
ISO11443
Pa·s
1
Impact performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5011
0°C
ASTMD256
J/m
4
0°C19
ISO180/1A
kJ/m²
5
23°C
ASTMD4812
J/m
4
23°C
ASTMD256
J/m
4
23°C
ISO179/2C
kJ/m²
6
23°C15
ISO179/1eA
kJ/m²
4
23°C17
ISO179/1eU,ISO179/2U
kJ/m²
4
23°C20
ISO180/1A
kJ/m²
6
23°C22
ISO180/1U
kJ/m²
4
-30°C
ASTMD4812
J/m
4
-30°C
ISO179/2U
kJ/m²
4
-30°C
ASTMD256
J/m
4
-30°C
ISO179/2C
kJ/m²
6
-30°C14
ISO179/1eA
kJ/m²
4
-30°C16
ISO179/1eU
kJ/m²
3
-30°C18
ISO180/1A
kJ/m²
5
-30°C21
ISO180/1U
kJ/m²
3
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
3
hardness
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5011
Ball pressure hardness
H358/30
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5011
Extreme Oxygen Index
ISO4589-2
%
2
Burning wire flammability index
1.00mm
IEC60695-2-12
°C
7
Burning wire flammability index
3.00mm
IEC60695-2-12
°C
8
Supplementary Information
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/VX5011
Filling material
ASTMD229
%
1