Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS NH-1013 K24806 Samsung Cheil South Korea
INFINO®
--
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/Samsung Cheil South Korea/NH-1013 K24806
Melt flow rate
220°C/10.0 kg
ASTM D1238, ISO 1133
g/10 min
3
Shrinkage rate
流动 : 3.20 mm
ASTM D955
%
0
Shrinkage rate
横向流动 : 3.20 mm
ASTM D955
%
0
Shrinkage rate
横向流量 : 2.00 mm
ISO 294-4
%
0
Shrinkage rate
流量 : 2.00 mm
ISO 294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/Samsung Cheil South Korea/NH-1013 K24806
Tensile strength
屈服 3
ASTM D638
Mpa
6
Tensile strength
屈服
ISO 527-2/50
Mpa
6
Tensile strength
断裂 3
ASTM D638
Mpa
5
Tensile strength
断裂
ISO 527-2/50
Mpa
5
elongation
断裂 3
ASTM D638
%
5
elongation
断裂
ISO 527-2/50
%
6
Bending modulus
-- 4
ASTM D790
Mpa
2
Bending modulus
-- 5
ISO 178
Mpa
2
bending strength
-- 4
ASTM D790
Mpa
9
bending strength
-- 5
ISO 178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/Samsung Cheil South Korea/NH-1013 K24806
RTI
1.5 到 3.0 mm
UL 746
°C
9
RTI Elec
1.5 到 3.0 mm
UL 746
°C
9
RTI Imp
1.5 到 3.0 mm
UL 746
°C
8
Vicat softening temperature
ISO 306/B50
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
8
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm
ISO 75-2/A
°C
8