Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI HU1010 7H1D395 SABIC INNOVATIVE NANSHA
ULTEM™
Medical and nursing suppl、Medical devices
Middle flow、Biocompatibility、Steam sterilization
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE NANSHA/HU1010 7H1D395
Melt volume flow rate
360°C/5.0kg
ISO1133
cm3/10min
2
Melt mass flow rate
337°C/6.6kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
1
Water absorption rate
平衡,23°C
ASTMD570
%
1
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE NANSHA/HU1010 7H1D395
Tensile strength 3
屈服
ASTMD638
Mpa
1
Tensile strength 3
断裂
ASTMD638
Mpa
1
Tensile modulus
ISO527-2/1
Mpa
3
Tensile modulus 2
ASTMD638
Mpa
3
Tensile strain
屈服
ISO527-2/5
%
6
Tensile strain
断裂
ISO527-2/5
%
6
Tensile stress
屈服
ISO527-2/5
Mpa
1
Elongation rate 3
屈服
ASTMD638
%
7
Elongation rate 4
断裂
ASTMD638
%
6
Taber abraser
1000Cycles,1000g,CS-17转轮
ASTMD1044
mg
1
Bending modulus
100mmSpan4
ASTMD790
Mpa
3
Bending modulus
50.0mm跨距5
ASTMD790
Mpa
3
Bending modulus 6
ISO178
Mpa
3
bending strength
屈服,50.0mm跨距5
ASTMD790
Mpa
1
bending strength
Yield,100mmSpan4
ASTMD790
Mpa
1
Bending strength 6,7
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE NANSHA/HU1010 7H1D395
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
RTIStr
UL746
°C
1
thermal conductivity
ASTMC177
W/m/K
0
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature 10
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
1
Vicat softening temperature
ASTMD152511
°C
2
Vicat softening temperature
--
ISO306/B50
°C
2
Vicat softening temperature
--
ISO306/B120
°C
2
Linear coefficient of thermal expansion
MD：-20to150°C
ASTME831
cm/cm/°C
5
Linear coefficient of thermal expansion
MD：-40到40°C
ISO11359-2
cm/cm/°C
5
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
5
Linear coefficient of thermal expansion
TD：-40到40°C
ISO11359-2
cm/cm/°C
5
Electrical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE NANSHA/HU1010 7H1D395
Dielectric strength
1.60mm,inAir
ASTMD149
KV/mm
3
Dielectric strength
1.60mm,在油中
ASTMD149
KV/mm
2
Volume resistivity
ASTMD257
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE NANSHA/HU1010 7H1D395
CharpyNotchedImpact Strength8
23°C
ISO179/1eA
kJ/m²
3
ReverseNotchIzodImpact
3.20mm
ASTMD256
J/m
1
Falling hammer impact
23°C
ASTMD3029
J
3
Suspended wall beam gap impact strength 9
-30°C
ISO180/1A
kJ/m²
5
Suspended wall beam gap impact strength 9
23°C
ISO180/1A
kJ/m²
5
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
3
flammability
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE NANSHA/HU1010 7H1D395
Extreme Oxygen Index
ASTMD2863
%
4