Density/specific gravity

ASTMD792

g/cm³

1

Density/specific gravity

ISO1183

g/cm³

1

Water absorption rate

24hr

ASTMD570

%

1

Water absorption rate

23°C,24hr

ISO62

%

1

Water absorption rate

饱和

ASTMD570

%

6

Water absorption rate

饱和,23°C

ISO62

%

6

Water absorption rate

平衡,50%RH

ASTMD570

%

1

Water absorption rate

平衡,23°C,50%RH

ISO62

%

1

Tensile strength

断裂,-40°C

ASTMD638

Mpa

2

Tensile strength

断裂,23°C

ASTMD638

Mpa

1

Tensile strength

断裂,80°C

ASTMD638

Mpa

1

Tensile strength

Break,121°C

ASTMD638

Mpa

8

Tensile modulus

-40°C

ISO527-2

Mpa

1

Tensile modulus

23°C

ISO527-2

Mpa

1

Tensile modulus

80°C

ISO527-2

Mpa

4

Tensile modulus

120°C

ISO527-2

Mpa

3

Tensile modulus

150°C

ISO527-2

Mpa

3

Tensile strain

断裂,-40°C

ISO527-2

%

3

Tensile strain

断裂,23°C

ISO527-2

%

3

Tensile strain

断裂,80°C

ISO527-2

%

7

Tensile strain

断裂,120°C

ISO527-2

%

7

Tensile strain

断裂,150°C

ISO527-2

%

6

Tensile stress

断裂,-40°C

ISO527-2

Mpa

2

Tensile stress

断裂,23°C

ISO527-2

Mpa

1

Tensile stress

断裂,80°C

ISO527-2

Mpa

1

Tensile stress

断裂,120°C

ISO527-2

Mpa

8

Tensile stress

断裂,150°C

ISO527-2

Mpa

8

elongation

断裂,-40°C

ASTMD638

%

3

elongation

断裂,23°C

ASTMD638

%

3

elongation

断裂,80°C

ASTMD638

%

7

elongation

Break,121°C

ASTMD638

%

7

Bending modulus

-40°C

ASTMD790

Mpa

9

Bending modulus

23°C

ASTMD790

Mpa

9

Bending modulus

65°C

ASTMD790

Mpa

4

Bending modulus

90°C

ASTMD790

Mpa

3

Bending modulus

121°C

ASTMD790

Mpa

3

Bending modulus

23°C

ISO178

Mpa

8

bending strength

-40°C

ASTMD790

Mpa

3

bending strength

23°C

ASTMD790

Mpa

2

bending strength

65°C

ASTMD790

Mpa

1

bending strength

90°C

ASTMD790

Mpa

1

bending strength

121°C

ASTMD790

Mpa

1

Bending stress

23°C

ISO178

Mpa

2

RTIElec

0.71mm

UL746

°C

1

RTIElec

1.5mm

UL746

°C

1

RTIElec

3.0mm

UL746

°C

1

Evolution Calendar intelligent importer

0.71mm

UL746

°C

1

Evolution Calendar intelligent importer

1.5mm

UL746

°C

1

Evolution Calendar intelligent importer

3.0mm

UL746

°C

1

RTIStr

0.71mm

UL746

°C

1

RTIStr

1.5mm

UL746

°C

1

RTIStr

3.0mm

UL746

°C

1

Hot deformation temperature

0.45MPa,未退火

ASTMD648

°C

2

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

2

Hot deformation temperature

1.8MPa,未退火

ASTMD648

°C

2

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

2

Melting temperature (DSC)

ISO3146

°C

2

Peak melting temperature

ASTMD3418

°C

2

Linear coefficient of thermal expansion

MD

ASTME831

cm/cm/°C

3

VolumeResistivity

1.50mm

ASTMD257

ohms·cm

>

Dielectric strength

IEC60243-1

KV/mm

4

Volume resistivity

IEC60093

ohms·cm

>

Charpy Notched Impact Strength

-30°C

ISO179

kJ/m²

1

Charpy Notched Impact Strength

23°C

ISO179

kJ/m²

1

Impact strength of simply supported beam without notch

23°C

ISO179

kJ/m²

8

Falling impact resistance

23°C

内部方法

J

4

Impact strength of cantilever beam gap

-40°C

ISO180

kJ/m²

8

Impact strength of cantilever beam gap

23°C

ISO180

kJ/m²

1

Impact strength of cantilever beam gap

-40°C

ASTMD256

J/m

1

Impact strength of cantilever beam gap

23°C

ASTMD256

J/m

1