Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT V4860HR BK1066 SABIC INNOVATIVE JAPAN
VALOX™
Automotive Applications、Lighting fixtures
Glass fiber reinforced、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE JAPAN/V4860HR BK1066
Density/specific gravity
ISO1183
g/cm³
1
Density/specific gravity
ASTMD792
g/cm³
1
Melt volume flow rate
250°C/5.0kg
ISO1133
cm3/10min
1
Melt mass flow rate
250°C/5.0kg
ASTMD1238
g/10min
1
Shrinkage rate
TD：3.20mm
内部方法
%
0
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE JAPAN/V4860HR BK1066
Fracture bending strain 8
ISO178
%
2
Tensile strength 3
断裂
ASTMD638
Mpa
1
Tensile strength 3
屈服
ASTMD638
Mpa
1
Tensile modulus
ISO527-2/1
Mpa
9
Tensile modulus 2
ASTMD638
Mpa
9
Tensile strain
屈服
ISO527-2/5
%
2
Tensile strain
断裂
ISO527-2/5
%
2
Tensile stress
断裂
ISO527-2/5
Mpa
1
Tensile stress
屈服
ISO527-2/5
Mpa
1
Elongation rate 3
屈服
ASTMD638
%
2
Elongation rate 4
断裂
ASTMD638
%
2
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
6
Bending modulus 5
ISO178
Mpa
7
Bending strength 4
屈服,50.0mm跨距
ASTMD790
Mpa
1
Bending strength 5
断裂,50.0mm跨距
ASTMD790
Mpa
2
Bending stress 5
--6
ISO178
Mpa
1
Bending stress 5
--7
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE JAPAN/V4860HR BK1066
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
2
Hot deformation temperature 11
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
ASTMD152512
°C
1
Linear coefficient of thermal expansion
TD：23to80°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：-40to95°C
ASTME831
cm/cm/°C
1
Linear coefficient of thermal expansion
MD：23到80°C
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
MD：-40到95°C
ASTME831
cm/cm/°C
2
Impact performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE JAPAN/V4860HR BK1066
CharpyNotchedImpactStrength9
23°C
ISO179/1eA
kJ/m²
1
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
9
Impact strength of cantilever beam gap
-30°C
ASTMD256
J/m
7
Suspended wall beam gap impact strength 10
23°C
ISO180/1A
kJ/m²
1
Suspended wall beam gap impact strength 10
-30°C
ISO180/1A
kJ/m²
8
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
1