Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 4012G SABIC INNOVATIVE US
VALOX™
Connector
Ductility、Fast forming cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/4012G
Density/specific gravity
ASTMD792
g/cm³
1
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
250°C/1.2kg
ISO1133
cm3/10min
9
Melt mass flow rate
250°C/1.2kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：--2
内部方法
%
0
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD2
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/4012G
FlexuralStrength5
Yield,50.0mmSpan
ASTMD790
Mpa
1
Tensile strength 4
屈服
ASTMD638
Mpa
7
Tensile modulus
ISO527-2/1
Mpa
4
Tensile modulus 3
ASTMD638
Mpa
4
Tensile strength 4
Break
ASTMD638
Mpa
7
Tensile strain
屈服
ISO527-2/5
%
4
Tensile strain
断裂
ISO527-2/5
%
4
Tensile stress
断裂
ISO527-2/5
Mpa
7
Tensile stress
屈服
ISO527-2/5
Mpa
7
Elongation rate 4
屈服
ASTMD638
%
3
Elongation rate 4
断裂
ASTMD638
%
3
Bending modulus 5
50.0mmSpan
ASTMD790
Mpa
3
Bending modulus 6
ISO178
Mpa
3
Bending strength 6,7
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/4012G
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 10
1.8MPa,Unannealed,100mmSpan
ISO75-2/Ae
°C
1
Hot deformation temperature 10
0.45MPa,Unannealed,100mmSpan
ISO75-2/Be
°C
2
Vicat softening temperature
ASTMD152511
°C
2
Vicat softening temperature
--
ISO306/B50
°C
2
Vicat softening temperature
--
ISO306/B120
°C
2
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
6
Linear coefficient of thermal expansion
MD：23到80°C
ISO11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
8
Linear coefficient of thermal expansion
TD：23到80°C
ISO11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
TD：23到150°C
ISO11359-2
cm/cm/°C
8
Electrical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/4012G
Surface resistivity
IEC60093
ohms
>
Dielectric strength
0.800mm,在油中
IEC60243-1
KV/mm
3
Dielectric strength
1.60mm,在油中
IEC60243-1
KV/mm
2
Dielectric strength
3.20mm,在油中
IEC60243-1
KV/mm
1
Leakage Trace Index
--
IEC60112
V
2
Leakage Trace Index
解决方案B
IEC60112
V
1
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/4012G
Impact strength of simply supported beam gap 8
-30°C
ISO179/1eA
kJ/m²
6
Impact strength of simply supported beam gap 8
23°C
ISO179/1eA
kJ/m²
7
Simple supported beam without notch impact strength 8
-30°C
ISO179/1eU
kJ/m²
4
Simple supported beam without notch impact strength 8
23°C
ISO179/1eU
kJ/m²
4
Unscented Izod Impact Strength 9
-30°C
ISO180/1U
kJ/m²
3
Unscented Izod Impact Strength 9
23°C
ISO180/1U
kJ/m²
3
Impact strength of cantilever beam gap
-30°C
ASTMD256
J/m
7
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
7
Suspended wall beam gap impact strength 9
-30°C
ISO180/1A
kJ/m²
6
Suspended wall beam gap impact strength 9
23°C
ISO180/1A
kJ/m²
6
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
4
hardness
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/4012G
Ball pressure hardness
H358/30
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE US/4012G
Burning wire flammability index
1.0mm
IEC60695-2-12
°C
7