Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PTFE DFL-4034 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and Electrical、Lighting applications
Easy to form、Easy to demould
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PTFE/SABIC INNOVATIVE US/DFL-4034
24hr,50%RH
ASTMD570
%
0
Balance, 23 ° C, 50% RH
ISO62
%
0
Shrinkage rate
MD:24小时
ASTMD955
%
0
Shrinkage rate
TD:24小时
ASTMD955
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PTFE/SABIC INNOVATIVE US/DFL-4034
--
ISO527-2/1
Mpa
6
--
ISO178
Mpa
1
--1
ASTMD638
Mpa
7
--5
ISO178
Mpa
6
50.0mm span 4
ASTMD790
Mpa
6
crack
ISO527-2/5
%
3
crack
ISO527-2/5
Mpa
9
Fracture, 50.0mm span 6
ASTMD790
Mpa
1
Fracture 2
ASTMD638
Mpa
9
Fracture 3
ASTMD638
%
2
Wear factor
Ring
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
1
Wear factor
Washer
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
8
yield
ISO527-2/5
%
2
Thermal performance
Test Condition
Test Method
Unit
PC/PTFE/SABIC INNOVATIVE US/DFL-4034
0.45MPa, unannealed, 3.20mm
ASTMD648
°C
1
0.45MPa, unannealed, 64.0mm span 9
ISO75-2/Bf
°C
1
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
1
1.8MPa, unannealed, 64.0mm span of 10
ISO75-2/Af
°C
1
Linear coefficient of thermal expansion
MD:-30到30°C
ASTMD696
cm/cm/°C
3
Linear coefficient of thermal expansion
TD:-30到30°C
ASTMD696
cm/cm/°C
6
Impact performance
Test Condition
Test Method
Unit
PC/PTFE/SABIC INNOVATIVE US/DFL-4034
--
ISO6603-2
J
6
23°C
ASTMD4812
J/m
7
23°C
ASTMD256
J/m
1
23°C,TotalEnergy
ASTMD3763
J
1
23°C7
ISO180/1A
kJ/m²
1
23°C8
ISO180/1U
kJ/m²
4